In present research six samples of nano X-type hexagonal ferrites with general formula SrBaMg2-xCoxDyyFe28-yO46 (x = 0–1; y = 0–0.1 with step size of 0.2 and 0.02, respectively) were synthesized by sol–gel technique. The temperature required for the phase formation of these materials was estimated using thermogravimetric analysis. X-ray diffraction patterns revealed the pure phase of the prepared materials up to the doping concentration of x = 0.4, y = 0.04 along with the second phase for higher doping concentration. The secondary phase appeared due to the solubility limit of higher ionic radius Dy3+ ions into the hexagonal lattice. The mean crystalline size decreased from 29 to 18 nm while... 

Gadolinium (Gd) and cobalt (Co) substituted Sr–Ba–Cu-based Y-type hexaferrites were synthesized with the help of the sol–gel auto-combustion route. XRD (X-ray diffraction) analysis was done to ratify the phase formation of hexaferrites. The impact of Gd3+ substitutions was measured on all the lattice parameters. Lattice constants “a” and “c” were found between 5.879–5.891 Å and 43.185–43.620 Å, respectively. It was observed from the XRD analysis that with an increase in Gd–Co contents, the enhancement in the average crystallite size is noted. The thermal decomposition process was studied using TGA (thermogravimetric analysis), revealing that the precursor may give the ending product when...