A novel biopolymer-based composite hydrogel was synthesized through chemical crosslinking by graft copolymerization of partially neutralized acrylic acid onto the carboxymethyl cellulose (CMC). The Taguchi method, a robust experimental design, was employed for the optimization of the synthesis based on the swelling capacity of the hydrogels. This method was applied for the experiments and standard L16 orthogonal array with five factors and four levels. In the synthesis of the composite superabsorbent, N,N'-methylene bisacrylamide (MBA) as crosslinker, ammonium persulfate (APS) as initiator, acrylic acid (AA) as monomer, CMC/Celite weight ratio and neutralization percent (NU) were used as... 

A novel biopolymer-based hydrogel composite was synthesized through chemical crosslinking by graft copolymerization of partially neutralized acrylic acid onto the hydrolyzed collagen. The Taguchi method, a robust experimental design, was employed for the optimization of the synthesis based on the swelling capacity of the hydrogels. This method was applied for the experiments and standard L16 orthogonal array with five factors and four levels. In the synthesis of the composite superabsorbent, N,N′-methylene bisacrylamide (MBA) as crosslinker, ammonium persulfate (APS) as initiator, acrylic acid (AA) as monomer, neutralization percent (NU), and collagen/kaolin weight ratio were used as... 

A series of superabsorbent composites were synthesized through graft copolymerization of acrylic acid (AA) onto carboxymethyl cellulose (CMC) in the presence of celite powder using N,N'-methylenebisacrylamide (MBA) as a cross-linking agent and ammonium persulphate (APS) as an initiator. The chemical structure and thermal properties of the composite hydrogels were characterized by FTIR spectroscopy and TGA methods, respectively. Morphology of the samples was examined by scanning electron microscopy (SEM). In free-state, the swelling conditions and hence the related data are not real, because in all their applications the swelling particles of superabsorbent must absorb aqueous solutions while...