Lanthanum chromite coating occupies a noticeable position as a ceramic coating on metallic interconnects in solid oxide fuel cells because of its excellent electrical conductivity, high oxidation resistance and desirable chemical stability in both oxidizing and reducing atmospheres. In the present work, a sol-gel process based on the dip-coating technique was used to prepare dense and uniform coatings on metallic alloy for interconnect application (AISI 430 type). The effect of strontium and calcium doping into lanthanum chromite structure on electrical conductivity and oxidation behavior of the coated sample has been investigated. The oxidation behavior was evaluated by cyclic oxidation... 

Abstract: The effect of de-siliconization on the oxidation behavior of AISI 430 stainless steel used for solid oxide fuel cell interconnect application was investigated. De-siliconization treatment was conducted via heating steel parts in an H2 environment. The de-siliconized substrates were then coated with a Mn1.5Co1.5O4 spinel coating, using wet spray method. For comparison, a similar coating process was applied on the as-received AISI 430 stainless steel specimens. Oxidation kinetics of coated interconnects were evaluated at 700, 800 and 900 °C in air. Results showed that the de-siliconization surface treatment decreased oxidation rates, with kinetic rates (g2 cm−4 s−1) of 4.39 × 10−14...