Solidification cracking is one the most common types of cracking in the weld of the aluminum alloys. Although some numerical models have been developed for investigation of the solidification cracking, the effect of the grain misorientation on the solidification cracking susceptibility (SCS) of a weld has rarely been considered. This work studies the effect of the angle between the primary arms of the dendrites on the SCS. Hence, a solidification cracking model was developed given the grain misorientation in the convergence condition. The model was investigated for Al-Cu alloys. When the grain boundary energy was considered in the model, there was an increase in the SCS for misorientation...