Antistatic Polyurethane Coating Containing Zirconia Nanoparticles
, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
In this study, antistatic waterborne polyurethane coating containing zirconia nanoparticles is made and applied on 304 stainless steel substrates at weight percentage of 0.66, 1.3, 3, 4.5 and 6% zirconia nanoparticles. For synthesis of hydrophilic isocyanate prepolymer, isocyanate prepolymer is modified by hydrophilic polyethylene glycol with molecular weight 600, 1000 and 4000. For ensuring of modification condition and stability of hydrophilic isocyanate prepolymer in aqua solution, FTIR and stability tests are employed, respectively. In order to create antistatic properties of these coatings, semi - conductive zirconia nanoparticles are used. To improve the distribution of zirconia...
Deposition and Properties of ZIF-8/SiO2 Hydrophobi Anti-Corrosion Coating
, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
In this research, a coating was created on the steel surface using the network structure of zeolite imidazolate-8 (ZIF-8) and its effect on the corrosion behavior of steel was investigated. Then, the effect of two coupling agents, mercaptopropyltriethoxysilane (MPTES) and aminopropyltriethoxysilane (APTES) on the coating and its anti-corrosion properties was investigated. Then, in order to make a hydrophobic coating, the substrate was first coated with ZIF-8 and then a combination of silica nanoparticles plus hexamethyldisilazane (HMDS) and polymethylhydrogensiloxane (PMHS) was added to the initial solution and then coating was done. As a result of this process, the contact angle of water...