Sharif Digital Repository

A seeding-growth approach was used to prepare Au@Ag@Au core double shell nanoparticles which were loaded on a rutile-nanorods/anatase-nanobranches thin film via the impregnation method. The thin film was synthesized on a fluorine-doped SnO 2 substrate via three stages of (i)TiCl 4 treatment, (ii)hydrothermal, and (iii)aqueous chemistry. The photocatalytic capability of the newly developed nanostructure was higher than P25 TiO 2 thin film by 40% under visible light and by 100% under UV light irradiation. Photogenerated charges separation at the junctions of rutile-nanorods and anatase-nanobranches along with localized surface plasmon resonance followed by the hot electron transfer from the... 

TiO2 nanotubes were synthesized using a modified autoclave-free thermal method from as-prepared initial powders. The size of initial powders (IP) was found to be critical in determining the morphology and crystal structure of the final product. Oleylamine (OA) was used as the polymer agent in the preparation of initial powders with different mol ratios of OA/Ti: 1, 5, and 10. X-ray diffraction analysis depicted that the increase of mole ratio up to 10 resulted in smaller nanoparticles with the sizes of about 8 nm. It was also deliberated that low temperature thermally treated IP showed the characteristic diffraction pattern of titanate phase of nanotubes. Scanning electron... 

Carbon nanotube (CNT)-doped TiO2 thin films with various CNT contents were synthesized by sol-gel method for visible light photoinactivation of Escherichia coli bacteria. Post annealing of the CNT-doped TiO2 thin films at 450 °C resulted in anatase TiO2 and formation of Ti-C and Ti-O-C carbonaceous bonds in the film. By increasing the CNT content, the thin films could further inactivate the bacteria in the dark. Meanwhile, as the CNT content increased from zero to 40 wt% the effective optical band gap energy of the CNT-doped TiO2 thin films annealed at 450 °C decreased from 3.2-3.3 to less than ∼2.8 eV providing light absorption in the visible region. Concerning this, visible light... 

A quantum modeling of the CO adsorption on illuminated anatase TiO2 (0 0 1) is presented. The calculated adsorption energy and geometries of illuminated case are compared with the ground state case. The calculations were achieved by using DFT formalism and the BH and HLYP. Upon photoexcitation, an electron-hole pair is generated. Comparing of natural population in the ground state and the exited state, shows that an electron is trapped in a Ti4+ ion and a hole is localized in an oxygen ion. The photoelectron helps generation of a CO2 molecule on the TiO2 surface. As shown by optimization of these systems, the CO molecule adsorbed vertically on the TiO2 (0 0 1) surface in the ground state... 

Graphene oxide platelets synthesized by using a chemical exfoliation method were deposited on anatase TiO2 thin films. Postannealing of the graphene oxide/TiO2 thin films at 400 °C in air resulted in partial formation of a Ti-C bond between the platelets and their beneath thin film. By using atomic force microscopy and X-ray photoelectron spectroscopy analyses, UV-visible light-induced photocatalytic reduction of the graphene oxide platelets of the annealed graphene oxide/TiO2. thin films immersed in ethanol was studied for the different irradiation times. After 4 h of photocatalytic reduction, the vertical space between the platelets decreased from about 1.1 to less than 0.8 nm and the... 

Hierarchical TiO 2 nanorod/nanoflower thin film was synthesized on fluorine doped tin oxide glass via hydrothermal and aqueous chemistry methods. According to field emission scanning electron microscopy results, the thin film was crack-free and uniform. Primary nanorods had an average diameter of 95 nm and a length of 2 µm. They were perpendicular to the substrate owing to the TiO 2 prenucleation. Growth of the nanoflowers on the nanorods could increase both the specific surface area and roughness. X-ray diffraction and Raman spectroscopy showed that the nanorods were rutile; while the nanoflowers were anatase. Efficient electron transfer from anatase to rutile could therefore occur.... 

In this investigation, the effect of annealing temperature and concentration of gold nanoparticles on the photoelectrochemical properties of sol-gel deposited Au : TiO2 nanocomposite thin films is studied. Various gold concentrations have been added to the TiO2 thin films and their properties are compared. All the deposited samples are annealed at different temperatures. The optical density spectra of the films show the formation of gold nanoparticles in the films. The optical bandgap energy of the Au : TiO2 films decreases with increasing Au concentration. The crystalline structure of the nanocomposite films is studied by x-ray diffractometry indicating the formation of gold nanocrystals in... 

The visible light photocatalytic activity of α-Fe2O3 nanograin chains coated by anatase TiO2 nanolayer, as a photocatalyst thin film for inactivation of Escherichia coli bacteria, was investigated for the solutions containing 106 colony forming units per milliliter of the bacteria, without and with H2O2 (60 μM). Thin films of the α-Fe2O3 nanograins with the grain size of 40-280 nm were grown on glass substrates by post-annealing of the thermal evaporated Fe3O4 thin films at 400 °C in air. The TiO2 layer with thickness of about 20 nm was coated on the nanograins by dipping the Fe2O3 thin films in a prepared TiO2 sol and re-annealing them at 400 °C in air. The antibacterial activity of the...