Sharif Digital Repository

In this work, a novel and facile synthesis process to fabricate single crystalline organometal halide perovskite nanowires has been successfully developed. Nanowires were grown in a high density ordered array from metal nanoclusters inside anodic aluminum oxide templates using a non-catalytic chemical vapor deposition method. Specifically, perovskite NWs were grown as a result of the reaction between methylammonium iodide (MAI) and the Pb/Sn (Pb or Sn) metal in anodic aluminum oxide templates under optimal conditions. The characterization results show that there is a reaction zone at the interface between the perovskite material and metal, at the bottom of the anodic aluminum oxide... 

Anodic aluminum oxide (AAO) was used as a template to prepare highly ordered Ni-Fe-Co alloy nanowire arrays. This membrane was fabricated with two-step anodizing method. It is found that there is an optimum barrier thickness to obtain a successful electrodeposition in pores of AAO. The thickness of barrier layer can be modified by additional electrochemical process after completing the anodizing step. Barrier layer thinning can create a rooted structure at the bottom side of the AAO pores and the electrodeposited nanowire arrays. The triple Ni-Fe-Co alloy was deposited in AAO membrane by ac voltage in a simple sulfate bath. The composition of nanowires shows anomalous deposition features... 

In this study, tensile strength of gypsum-based composite with aluminum fibers up to 15 vol.% was studied. To increase the interfacial bond strength between fibers and matrix, aluminum fibers were anodized under different conditions. Single fiber pull-out tests were carried out to investigate the bond strength. The interface was examined by scanning electron microscope. The ability of the composites to withstand longitudinal tensile load was also studied by tensile tests of dog bone-shaped, randomly oriented fiber-reinforced gypsum. By the introduction of aluminum fibers in gypsum as a randomly oriented composite, considerable increment in the strength is achieved and the toughness of the... 

This work studies the electrochemical growth behavior of cobalt nanowires in highly ordered aluminum oxide membrane. Considering the electrodeposition of metallic nanowires, cation concentration profile in each nano pore was calculated. With assumption of linear diffusion zone on the growing surface of nanowires, a modified Cottrell equation was evaluated. To confirm the model, the Co nanowires were electrodeposited into porous anodic aluminum oxide (AAO) templates and the mechanism of deposition was studied. Comparing the results of model and the experiments has proved the accuracy of the model. Also, it was observed that the growth of the Co nanowires was controlled mainly by diffusion... 

This paper presents solid-state ligand exchange of spin-coated colloidal lead sulfide quantum dot (PbS QD) films by methylammonium iodide (MAI) and integration of them in depleted heterojunction solar (DHS) devices having an antireflecting (AR) nanocone plastic structure. Time-resolved photoluminescence measurements determine a shorter lifetime of the charge carries on a semiconductor (TiO2) electron transfer layer for the MAI-passivated QD films as compared with those with long-chain aliphatic or short thiol ligands. Consequently, the DHS device yields improved power conversion efficiency (>125%) relative to oleic-acid-passivated PbS QD films. Using anodized aluminum oxide templates, an... 

This study shows the growth behavior of Co-Ni alloy nanowires in AAO template. Growth of nanowires consists of four different stages namely electronucleation, steady state growth, filling of pores, and coverage of filled nanowires and forming of a film on the template surface. TEM study of nanowires showed that the nanowires possess hemispherical head due to the preferable and more rapid growth phenomenon in central section of nanowires instead of edge sides. Studies on the relations between nanowires composition and ion concentration in solution showed that growth of nanowires is a diffusion-controlled process. The compositional, structural and magnetic properties of nanowires were... 

Room temperature gas sensing behavior of arrayed one-dimensional (1D) nickel nanowires (Ni NWs) are investigated using impedance spectroscopy. Ni nanowires synthesized via electrochemical deposition method based on anodic aluminum oxide (AAO) templates. Their structural characterization verified by scanning electron microscopy (SEM), x-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR) analysis. Impedance spectroscopy as an essential technique utilized to understand the mechanism of gas interaction with the wires through the changes in their electronic behavior. Bode and Nyquist plots with the real and imaginary impedances are plotted versus frequency range of 500 Hz...