Dolomite base refractories have advantages such as high refractoriness, potential to produce pure steel molten, high alkaline corrosion resistance, and economical for consumers. However, application of these refractories has been limited due to their high potential to hydration with atmosphere humidity. In this research work, the impact of ZrSiO4 nanoparticles addition on the physical, thermo-mechanical, mechanical, and microstructure of the dolomite base refractories is investigated. Also, XRD and SEM/EDX analyses were used for determining generated ceramic phases and microstructure evaluation, respectively. Up to 3 wt% ZrSiO4 nanoparticles were added to the compositions. Compositions fired... 

In this work the effect of nano- and microZrO2 addition on the densification and hydration resistance of MgO–CaO refractories was investigated. 0, 2, 4, 6 and 8 wt% ZrO2 was added to MgO–CaO refractories that contain 35 wt% CaO. The crystalline phases and microstructure characteristics of specimens sintered at 1650 °C for 5 h in an electric furnace were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The physical properties are reported in terms of bulk density, apparent porosity and hydration resistance. Results show that with addition of ZrO2 the bulk density and hydration resistance of the samples increased while apparent porosity decreased. Also...