The creep behavior of particulate Al-5vol.% SiC composite was investigated. The composite powder was produced by mechanical milling and hot extruded at 450°C at the ratio of 16:1. A creep test was carried out at a constant load at 598, 648, and 673 K. Using the existing equations proposed for the steady-state creep of metals, the threshold stress and the stress exponent of the creep as a function of temperature were determined. The stress exponent was found to be 3 at the temperature of 673 K and 8 at the lower temperatures, i.e. 598 and 648 K. The dependency of the threshold stress to temperature obeys the Arrhenius relationship with the energy term of 29 kJ mole-1  

V2O5/SiO2 catalyst utilized to oxidize the SO2 to SO3 species in the presence of oxygen mainly for producing sulfuric acid. For this catalyst, the active phase was a mixture of vanadium pentoxide and basic sulfate/pyrosulfate material. This active phase at the reaction temperature behaved as a liquid filling up the pores of the silica support. On the other hand, amounts of the SO3 and V5+ species in the catalyst necessarily varied with the concentration of the feed material and temperature rendering complexity to the kinetics of the SO2 oxidation reaction. In the current research, the catalyst preparation with different amounts of such materials was undertaken. Purified Diatomaceous earth of... 

In precipitation hardenable materials, it is desirable to determine the precipitate dissolution temperature for homogenizing the microstructure by controlling the size and distribution of the precipitates. In this research, the influence of various heat treatment and hot deformation conditions on the kinetics of γ ′ dissolution and its morphological evolution in Nimonic 115 was studied. In addition, hot deformation behavior of the material was investigated using hot compression experiments at varying temperature (between 1,050°C and 1,175°C) and strain rates (between 0.01 and 1 s-1) up to a true strain of 0.8. The values obtained for the solvus temperature of γ ′ precipitates by two methods... 

Inkjet printing of colloidal metals is an attractive method for direct patterning of electrically conductive structures and interconnects in electronic devices, owing to low-cost, low-waste and simplicity of the process. In the present work, mixtures of well-dispersed silver nanoparticles and ethylene glycol were prepared for the inkjet printing process. Three different surfactants including PVP, MSA and AOT were added to study the stability of the nanosilver colloids. The effect of high-intensity ultrasonic treatment and temperature on the rheological properties was investigated utilising a rheometer in plate-plate geometry. It is shown that the viscosity of the ink increases with...