Alumina-MWCNT composite was densified by microwave sintering. CNTs were coated with boehmite nanoparticles to enhance their distribution in composite samples. Calcination temperature of composite powder was determined by TGA analysis (5 °C/min). Samples containing 0 and 1vol%CNT were produced by cold isostatic pressing at 180 MPa. Microwave sintering (1520 °C for 45 min) was conducted under the flow of argon. Phase analysis of the calcined composite powder showed complete transformation of boehmite into gamma-alumina. The relative densities were 99.3% and 98.1% for monolithic alumina and composite, respectively. CNT addition improved the fracture toughness of alumina by ~37%. SEM images... 

In this study hydroxyapatite (HA)/zirconia/alumina composite coatings on titanium metal was carried out using Sol-Gel dip coating and calcination process. Hydroxyapatite-Alumina-Zirconia sol, coated samples in three processes by changing final sol stirring time, aging time, calcination temperature of synthesized powder and prepared coating and rate of coating. Some parts of prepared sol were also synthesized and became powder in all three processes. Scanning electron microscopy was used to estimate the particle size of the surface and for morphological analysis. The functional group and crystallization characteristics of the powders were analyzed using (FTIR) and X-Ray diffraction (XRD)....