Sharif Digital Repository

Nanostructured molybdenum oxide was potentiodynamically deposited onto a stainless steel surface from an aqueous bath by cycling the potential between 0 and -0.75 V vs. Ag/AgCl. The deposit consisted of particulates in the range of 30 to 80 nm. Electrochemical studies under galvanostatic charge/discharge and also impedance spectroscopy revealed capacitive behavior in the potential range of -0.3 to -0.55 V vs. Ag/AgCl with the value of 477 F g-1 at 0.1 mA/cm2. An equivalent circuit comprising of three parallel branches consisting of double-layer capacitance, Warburg impedance, and a constant phase element signifying pseudo-capacitance each coupled with their corresponding resistances was... 

Nanostructured molybdenum oxide having a particle size in the range of 30-80 nm was prepared by potentiodynamic electrodeposition method, and the effects of H2SO4 concentration on its capacitive behavior were studied by cyclic voltammetry, galvanostatic discharge, and electrochemical impedance spectroscopy. Poor to fair capacitive behaviors were witnessed depending on the electrolyte concentration and conditions of charge/discharge. Increasing acid concentration to 0.02 M had favorable effect, while beyond that, the effect was detrimental. Capacitance around 600 F g-1 was recorded in the potential range of 0 to -0.55 V vs. Ag/AgCl  

Three-dimensional macroporous fluorine-doped tin oxide (p-FTO) films were successfully deposited using commercial ink of FTO powder and SnCl2 salt via Dr. Blade method. Various features of p-FTO thin films were studied as a function of the ink composition and sintering temperature. The morphological studies corroborated formation of porous, uniform, and crack-free FTO films after annealing at 300 °C for 10 min in air. X-ray diffraction pattern demonstrated development of highly crystalline FTO films. The lowest sheet resistance of 47 Ω/□ was obtained for the p-FTO film with a thickness of 21 μm. The capacitance of thin p-FTO films was investigated using a three-electrode system and the... 

Agglomerates of tungsten trioxide in the range of 90 nm to 1 μm are prepared by the acid precipitation method and characterized by XRD as well as scanning electron microscopy. The product when coated with platinum showed pseudocapacitance when in contact with acidic electrolyte in the potential range of 0. 1 to -0. 25 V/SCE. Capacitance in the range of 0. 014 to 0. 039 F cm-2 exhibiting moderate potential dependencies measured through both chronopotentiometry and impedance spectroscopy is presumed to be due to the insertion/de-insertion of protons into the lattice of tungsten trioxide. Equivalent circuit consisting of parallel simulators of mass transfer and capacitor charging... 

Three-dimensional macroporous fluorine-doped tin oxide (p-FTO) films were successfully deposited using commercial ink of FTO powder and SnCl2 salt via Dr. Blade method. Various features of p-FTO thin films were studied as a function of the ink composition and sintering temperature. The morphological studies corroborated formation of porous, uniform, and crack-free FTO films after annealing at 300 °C for 10 min in air. X-ray diffraction pattern demonstrated development of highly crystalline FTO films. The lowest sheet resistance of 47 Ω/□ was obtained for the p-FTO film with a thickness of 21 μm. The capacitance of thin p-FTO films was investigated using a three-electrode system and the...