In this research, we have used glancing angle deposition (GLAD) RF sputtering technique with various angular speeds ranging from 5 to 30 RPM to fabricate polytetrafluoroethylene (PTFE, Teflon) coated Tungsten on glass substrate for producing hydrophobic surface. According to scanning electron microscopy (SEM) observations, Tungsten nanorods were formed on the substrate with average diameter and length of about ∼50 nm and 300 nm, respectively. Hydrophobic property of W/Glass and PTFE/W/Glass systems was investigated by water contact angle measurements and we have found that the contact angle varied with the substrate angular speed. Maximum contact angle of 121 was measured for the... 

In this research, initially anodization process was used to fabricate ZnO nanorods on Zn substrate and then RF sputtering technique was applied to grow a thin layer of polytetrafluoroethylene (PTFE, Teflon) on the coated ZnO nanorods for producing a superhydrophobic surface. According to scanning electron microscopy (SEM) observations, ZnO nanorods were formed with average diameter and length of about ∼180 nm and 14 μm, respectively. Superhydrophilic property of ZnO nanorods and superhydrophobic property of PTFE/ZnO nanorods was investigated by water contact angle (WCA) measurements. It was found that the contact angle varied with the PTFE deposition time. The highest contact angle...