Tissue engineering and regenerative medicine have solved numerous problems related to the repair and regeneration of damaged organs and tissues arising from aging, illnesses, and injuries. Nanotechnology has further aided tissue regeneration science and has provided outstanding opportunities to help disease diagnosis as well as treat damaged tissues. Based on the most recent findings, magnetic nanostructures (MNSs), in particular, have emerged as promising materials for detecting, directing, and supporting tissue regeneration. There have been many reports concerning the role of these nano-building blocks in the regeneration of both soft and hard tissues, but the subject has not been... 

In order to evaluate the long-term viability, the iron content stability, and the labeling efficiency of mammalian cells using magnetic cell labeling; dextran-coated ultrasmall superparamagnetic iron oxide (USPIOs) nanoparticles with plain surfaces having a hydrodynamic size of 25 nm were used for this study. Tests were carried out in four groups each containing 5 flasks of 5.5 × 10 6 AD-293 embryonic kidney cells. The cell lines were incubated for 24 h using four different iron concentrations with and without protamine sulfate (Pro), washed with phosphate-buffered saline (PBS) and centrifuged three times to remove the unbounded USPIOs. Cell viability was also verified using USPIOs. There... 

In the present study, first, Fe3O4nanoparticles were functionalized using glutaric acid and then composited with CQDs. Doxorubicin (DOX) drug was loaded to evaluate the performance of the nanocomposite for targeted drug delivery applications. The XRD pattern confirmed the presence of characteristic peaks of CQDs and Fe3O4. In the FTIR spectrum, the presence of carboxyl functional groups on Fe3O4/CQDs was observed; DOX (positive charge) is loaded onto Fe3O4/CQDs (negative charge) by electrostatic absorption. FESEM and AFM images showed that the particle sizes of Fe3O4and CQDs were 23-75 and 1-3 nm, respectively. The hysteresis curves showed superparamagnetic properties for Fe3O4and Fe3O4/CQDs...