An approach for calculating weld efficiency from the results of a peel test has been developed for 5754-aluminum strips. The method is based on estimating the effective load-bearing area of peel test specimens. A convincing agreement between the results and the theoretical model-earlier developed by Wright et al. (Metals Technol. 5 (1978) 24)-has been found. The influence of surface expansion and rolling pressure on the weld efficiency has been studied by the new approach. © 2002 Elsevier Science B.V. All rights reserved  

In this research, it is shown that the production of bimetallic Al/Cu rod by cold ECAE process is feasible. The mechanism of the cold weld between the copper sheath and aluminum core is assessed using the characteristics of the mating surfaces both theoretically and by examining the SEM micrographs of the peeled surfaces. It is shown that the stretch produced by the shear strain in the process leads to the fracture of the work-hardened layer of the mating surfaces and then by extruding the virgin metal through the cavities of the cracks a cold weld is developed between the sheath and core of the rod. To achieve the cold weld, a threshold surface stretch of about 59% is required. It is shown... 

In this research, the application of equal channel angular extrusion process to produce both the cold-welded and diffusion-bonded Al/Cu bimetallic rods is assessed. The joints shear strength for both of the methods are measured and compared. The microstructure examinations were also carried out using scanning electron microscope equipped with EDX system and x-ray diffraction analysis. The results exhibit that the strength of the bond in cold-welded specimens is dependent on the amount of stretch and pressure at the materials interface. But in the diffusion-bonded specimens, it is depended on the struggle between the oxidation rate of the mating surfaces accompanied by inter-metallic...