In this work, the effect of zircon content on the mechanical and chemical behaviors of injection molded silica-based ceramic cores has been investigated. In order to simulate a casting process condition, the sintered samples at 1220 C were consequently heated up to 1430 C. Three point bending tests were carried out on all the prepared samples. The chemical resistance of the prepared cores was evaluated by leaching of samples in 43% KOH solution at its boiling point. Phase evolution and microstructure were investigated by XRD and SEM, respectively. Results showed that increasing zircon content led to an increase in MOR and decrease in leachability owing to the decrease in content of fused... 

In this work, cristobalite crystallization and its effects on mechanical and chemical behaviour of injection moulded silica-based ceramic cores were investigated. In order to simulate casting process condition, the sintered samples at 1220 °C were also heated up to 1430 °C. Flexural strength test was carried out on both sintered and heat treated samples. Chemical resistance of the cores was evaluated by leaching the samples inside 43. wt% KOH solution at its boiling point. Phase evolution and microstructure were investigated by thermal analyses (DTA and DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM) and optical microscopy (OM). Results showed that cristobalite was... 

The objective of this study was to evaluate the effects of P 2O5 particle size distribution on the crystalline phases and microstructure of lithium disilicate glass-ceramics derived from the TiO2-ZrO2-Li2O-CaO-Al2O 3-SiO2 system for dentistry applications. The samples were made via fusion and casting procedure. Crystallisation as well as the morphology and microstructure of the samples were investigated using X-ray diffraction, differential scanning calorimetric and scanning electron microscopy. The results showed that the crystallisation of the samples occurred in the range of 500-650°C. The main crystalline phase was lithium disilicate (Li2Si2O5) along with Lithium metasilicate (Li2SiO3),... 

The effects of SiO 2 and K 2O were investigated on the glass forming ability (GFA) and structural characteristics of CaOTiO 2P 2O 5 system. Differential thermal analyzer (DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM), FT-IR and 31P magic angle spinning NMR methods were applied for characterizations of the system. Unwanted crystallization in the initial three components base glass composition was observed by adding SiO 2 and crystalline phases such as TiP 2O 7, rutile (TiO 2) and cristobalite (SiO 2) were formed in it. The results showed that K 2O prevents crystallization of glasses and promotes the formation of glass. FT-IR and X-ray diffraction showed that the addition...