In present research, nanocrystalline Fe100-xSix (x = 6.5, 10, 13.5, 20 and 25 at.%) and Fe83.5Si13.5Nb3 alloy powders were prepared by mechanical alloying using high-energy ball milling. The resulting powders mainly consist of micron-sized particles with an average grain size of less than 20 nm. According to the XRD test results, by increasing the milling time and/or the Si content the lattice parameter decreases and the internal microstrain increases. In addition, the specific saturation magnetization diminishes as Si content increases. The coercive forces of the as-milled nanocrystalline powders are much higher than those of corresponding Fe-Si bulk alloys with a minimum at 13.5 at.% Si....