Sharif Digital Repository

In current studies, equal channel angular pressing process (ECAP) and modified ECAP processes are simulated under ideal conditions to compare the deformation characteristics. The deformation behaviour is more complicated and the strain induced during the processes is highly non-uniform in the modified ECAP processes except in the equal channel multi-angular pressing (ECMAP) process with Route C. The strain homogeneity is more of a possibility with ECAP and ECMAP with Route C processes. The deformation stress state is widely distributed in nature in modified ECAP processes than in conventional ECAP. In addition, the load requirements are also higher in modified ECAP processes with that of the... 

Simple compression and microscopy techniques were employed to characterise the microstructural origin of the deformation behaviour of nickel base superalloy IN625 during large strain testing. The alloy exhibited a four-stage strain hardening response similar to that previously reported for low stacking fault energy face centred cubic alloys. At strains lower than about -0.06 (stage A), a falling regime of the hardening rate was observed. This stage was followed by a second stage (stage B) of slow increasing hardening rate, which was found to be coincident with the formation of Lomer-Cottrell locks. The second falling regime of strain hardening (stage C) was seen in the strain range of -0.25... 

In this study, hot extrusion of AA6061-5% SiCp composite was studied to determine the composite thermo-mechanical behaviour during deformation and the mechanical properties of extruded composite. Hot compression tests were first carried out to obtain the flow stress behaviour of the composite at different temperatures and strain rates. Then a mathematical model was used to estimate the required energy as well as to predict temperature and strain distributions during the process. Finally, hot extrusion experiments were performed in order to verify the predictions and, also, tensile and hardness testing were conducted to evaluate mechanical properties of extruded material. Comparison between... 

Hot deformation behaviour of as-extruded Al-5vol% Al 2O 3 nanocomposite was investigated at temperatures range 350 to 450°C and initial strain rates of 5.5 × 10 -4 to 10 -1 s -1 and compared with those of monolithic (unreinforced) aluminium. Both extruded materials exhibited work-softening during hot deformation. The results showed that with the addition of 5 vol% alumina nanoparticles with an average particle size of 35 nm, a significant increase in compressive strength of aluminium was obtained. For instance, at 350°C an abrupt rise of ∼340% in hot strength of the nanocomposite relative to monolithic aluminium was achieved. TEM investigation of microstructure of the nanocomposite after hot... 

Compression test was used to study the deformation behaviour of sintered (12% porosity) and powder extruded (1% porosity) Al6061 alloy at high temperatures ranging from 350 to 500°C. The flow curves of the materials were determined at strain rates of 0.001, 0.01 and 0.1 s-1. The extruded alloy exhibited plastic instability in the form of bulging and formation of shear bands. The deformation activation energy of the extruded material was determined to be QI=77±16 kJ mol-1 (T<450°C) and OII=136±12 kJ mol-1 (T≥450°C). The values of activation energy and appearance of strain softening in the stress-strain curves revealed that thermally activated restoration processes, i.e. dynamic recovery and... 

Different experimental techniques which have been developed to obtain data related to force-deformation behaviour of soft tissues play an important role in realistically simulating surgery processes as well as medical diagnoses and minimally invasive procedures. Indeed, an adequate quantitative description of soft-tissue-mechanical-behaviour requires high-quality experimental data to be obtained and analysed. In this review article we will first scan the motivations and basic technical issues on surgery simulation. Then, we will concentrate on different experimental techniques developed for recording force-deformation (stress-strain) behaviour of soft tissues with focussing on the in-vivo...