Sharif Digital Repository

TiO2 nanoparticles were synthesized by hydrothermal assisted sol-gel technique. The preparation parameters including pH value, the amount of water, titanium tetra isopropoxide content, temperature and time of hydrothermal process were investigated by Taguchi statistical experiments to determine the influence of synthesizing variables on the optimal conditions and to realize the highest degree of crystallinity or smallest crystallite size. X-ray diffraction (XRD) analysis and direct band gap energy (Eg) values, measured via diffuse reflectance spectra (DRS), proved that all the samples consist of anatase as a unique phase. Transmission electron microscopy (TEM) and specific surface area... 

In this research, an attempt was made to improve TiO2 photo-catalyst properties, thus pure, N-Ce co-doped TiO2 thin films were prepared on glass-ceramic substrate using a sol-gel dip-coating technique. The samples were calcinated in air at 475 °C, 550°C, and 650°C for 2 h. The result of simultaneous thermal analysis (STA) and X-ray diffraction (XRD) showed that the presence of Ce in TiO2 could inhibit the phase transformation from anatase to rutile and enhance the thermal stability, and anatase was the dominant phase in N-Ce co-doped TiO2 samples. Also based on the results, the doping results in decreasing the size of TiO 2 crystallite. The results of ultra violet-visible light diffuse... 

An easy method for preparing CuO nanoparticles incorporated in a mesoporous structure was presented based on the thermal decomposition of a copper complex. The novel copper coordination compound of [Cu(anic)2]·0.75H2O (anic= 2-aminonicotinate) with the microflake morphology was synthesized through the reaction of 2-aminonicotinic acid (Hanic) and copper(II) nitrate. Using elemental analysis and Fourier transform infrared (FTIR) spectroscopy, the chemical composition of CuC12H11.5N4O4.75 was proposed. Calcination process at 550 °C for 4 h transformed the microflakes into CuO nanoparticles incorporated in a mesoporous structure. The FTIR peaks assigned to 2-aminonicotinate were completely... 

The structural, electrical, optical, and photovoltaic properties of aggregated submicron nitrogen-doped TiO2 particles (NTiO2) and the influence of utilizing them, in comparison with undoped ones, as the light-scattering layer of dye-sensitized solar cells were investigated. Field emission scanning electron microscope, X-ray diffraction, and diffuse reflectance spectra showed that both type samples have similar morphology, crystal phase, and scattering feature. Moreover, photoluminescence, Mott–Schottkey, and photovoltaic characteristics such as IMPS/IMVS and charge extraction analysis indicated that the NTiO2 layer is an efficient scatterer in two aspects: enhancement of light-harvesting... 

Herein, we demonstrate a facile low temperature chemical bath deposition approach to deposit a light scattering layer on a nanostructured mesoporous TiO2 bottom layer in a dye-sensitized solar cell architecture. Large TiO2 nanoparticles were formed on the top surface of photoanode electrodes via hydrolysis of TiCl4 at 70 °C. We controlled the size and agglomeration of these TiO2 nanoparticles by altering the concentration of TiCl4 in the chemical bath during the hydrolysis process. Electron microscope images revealed that mono-dispersed scattering particles having uneven surfaces with diameters between 100 to 300 nm formed on the mesoporous titania layer. The scattering behavior of the...