Sharif Digital Repository

Very fine alumina nanoparticles were loaded in novolac type phenolic resin (PF) using solution mixing method. The concentration of nanoalumina in PF was varied between 2.5 to 20 wt%. All the compounds were compression molded and then subjected to scanning electron microscopy (SEM), tensile, flexural, and dynamic mechanical analysis (DMA) tests. SEM analysis showed that the nanoalumina were dispersed uniformly at low concentrations, however, at high concentrations, dispersion was suppressed leading to agglomerates in the composites. Mechanical testing revealed that the nanoalumina had a great influence on the strength and stiffness of PF resin particularly at concentrations below 5 wt%.... 

The reinforcing effect of high structure carbon black (HSCB) and multi-walled carbon nanotubes (MWCNTs) on natural rubber/styrene-butadiene rubber blend processed using mechanical mixing was comparatively investigated. In-depth analysis by dynamic mechanical analysis, the Eggers-Schummer model and Medalia's relationship showed that HSCB aggregates provided large internal pores leading to significant immobilized macromolecules in filled rubber. Additionally, a tubular immobilized rubber layer with a thickness of 8nm was estimated for the rubber/MWCNT system based on dynamic mechanical analysis data. The mechanical performance of the HSCB filled blend was higher than that of the MWCNT filled... 

The phenolic-based brake friction composites containing 0, 1, 2 and 4 vol% carbon fiber were fabricated in this study. Thermogravimetric analysis (TGA) revealed the adverse impact of carbon fiber on the thermal stability of the composites under air atmosphere. Differential scanning calorimetry (DSC) of the uncured samples indicated the positive impact of carbon fiber on the crosslink density of the phenolic resin. Viscoelastic results drawn from the dynamic-mechanical analysis (DMA) suggested that inclusion of carbon fiber increased the storage modulus and decreased the damping factor of the frictional composites. The tribological behavior of the specimens was assessed with a chase type... 

Reinforcement of rubbery materials with carbon nanotube (CNT) has gained much attention over the last few decades due to the inherent ability of CNT to improve the physical and mechanical properties of polymer composites. However, CNT renders electrical conductivity to the rubber composites, which could be problematic for a number of applications. In an attempt to overcome such issues, we controlled the insulating properties of styrene-butadiene rubber (SBR) nanocomposites by hybridization of CNT with nanodiamond (ND) particles without scarifying desirable features of the nanoparticles. In this respect, the effects of carbon nanotube (CNT) and nanodiamond (ND), either individually or in... 

A series of biodegradable acrylic terminated polyurethanes (APUs) based on poly(ε-caprolactone) diol (PCL), aliphatic 1,6-hexamethylene diisocyanate (HDI) and hydroxyethyl methyl acrylate (HEMA) was synthesized as potential materials for hard tissue biomedical applications. PCLs with low molecular weights of 1000 and 2000 g/mol were employed to provide different amounts of end capped urethane acrylate in APUs. To control crosslink density, a mixture of two different reactive diluents including mono-functional HEMA and bi-functional ethylene glycol dimethacrylate (EGDMA) with different weight ratios was incorporated into the APUs, called here PUAs. Morphological characteristics and mechanical...