Sharif Digital Repository

Commercial pure copper sheets were severely deformed after primary annealing to a strain magnitude of 2.32 through constrained groove pressing. After induction of an electrical current, the sheets were heated for 0.5, 1, 2, or 3 s up to maximum temperatures of 150, 200, 250, or 300°C. To compare the annealing process in the current-carrying system with that in the current-free system, four other samples were heated to 300°C at holding times of 60, 90, 120, or 150 s in a salt bath. The microstructural evolution and hardness values of the samples were then investigated. The results generally indicated that induction of an electrical current could accelerate the recrystallization process by... 

In this work, the electrokinetic properties of asphaltene particles have been investigated. Micro-electrophoresis method by applying DC electric field, was utilized to different mixtures containing asphaltene to determine its electric charge. It was observed that in the case of using n-heptane and its mixture with toluene (heptol), the asphaltene particles were showed to be positively charged however for toluene itself, they expressed no tendency toward the electrodes. While it is expected that larger asphaltene aggregates carry higher electric charge, the results contradictorily showed that they are mainly governed by gravity rather than electro-static force and that “aggregation” reduces...