Cathodically deposited Ag 2Se, to form a 1-μm-thick film, characterized by energy dispersive X-ray analysis and scanning electron microscopy, showed high electro-catalytic activity for l-ascorbic acid oxidation in alkaline solution. The onset of the process was about 80 mV cathodic of that previously observed on Ag under the same conditions and far superior over glassy carbon and Pt. The values of the exchange current density, standard heterogeneous rate constant, and transfer coefficient of the reaction were 1. 65 × 10 -4 A cm -2, 4. 35 × 10 -7 cm s -1, and 0. 60, respectively. Diffusion coefficient of l-ascorbate di-anion was also measured and was around 7. 00 × 10 -6 cm 2 s -1  

Ni/SiC nanocomposite coatings were electrodeposited using Watts type bath and different SiC particle size. The electrodeposition behavior of Ni/SiC nanoelectrocomposites was studied using electrochemical techniques such as impedance spectroscopy (EIS) and voltammetry. In this study it was shown that SiC particles modify the EIS diagram and voltammograms as well as surface morphology of electrodeposited layers. Experimental results showed that SiC particles not only affect the formation of intermediate species and decrease charge transfer resistance but also increase the nucleation sites for nickel electrodeposition and thus affect the microstructure of electrodeposited Ni/SiC nanocomposites.... 

The effect of electrostatic field on the aggregation rate and aggregate size of asphaltene particles precipitated from three different crude oil samples suspended in a mixture of toluene and n-heptane (a model oil) was investigated. An electrode-embedded glass micro-model utilizing a high-voltage direct current power supply was utilized in this study. The asphaltene particle size and the rate of aggregation under the electric field were monitored using a high-resolution optical microscope and the average aggregate size for asphaltene particles was estimated using image processing software. To investigate the effects of structural parameters on asphaltene aggregation rate, aggregate size and... 

The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the cathodic current density. The composition, surface morphology, roughness, layers growth pattern as well as the phase structure of deposits were extensively studied via SEM, EDS, AFM and XRD analysis. Effects of bath ingredients on the electrodeposition behavior were analyzed through cathodic linear sweep voltammetry. Although the concentration of Zn2+ in bath was 13 times higher than Ni2+, the Zn-Ni deposition potential was much nearer to Ni deposition potential rather than that of Zn. Addition of NaH2PO2 to the Ni deposition bath considerably raised the current...