Sharif Digital Repository

Ordered perpendicular TiO2 nanotubes (TNT) with 405 to 952 nm length and 60 to 90 nm diameter were grown via 40 to 120 min anodization of Ti6Al4V flat substrates. The samples were called TNT-40, -60, -80, -100, and -120. Vancomycin was loaded on the bare and anodized electrodes by separate immersion and electrophoretic (EP) deposition procedures. EP loading resulted in storage capacity of 5221.86 μg cm-2 for TNT-80 which was much higher than 1036.75 μg cm-2 of immersed sample. Drug release comprised of three stages: (i) burst release (78% for the bare, and 23% for the TNT-80 sample), (ii) gradual transport (21% for the bare, and 64% for the TNT-80 sample), and (iii) equilibrium. Transfer... 

Ordered perpendicular TiO2 nanotubes (TNT) with 405 to 952 nm length and 60 to 90 nm diameter were grown via 40 to 120 min anodization of Ti6Al4V flat substrates. The samples were called TNT-40, -60, -80, -100, and -120. Vancomycin was loaded on the bare and anodized electrodes by separate immersion and electrophoretic (EP) deposition procedures. EP loading resulted in storage capacity of 5221.86 μg cm-2 for TNT-80 which was much higher than 1036.75 μg cm-2 of immersed sample. Drug release comprised of three stages: (i) burst release (78% for the bare, and 23% for the TNT-80 sample), (ii) gradual transport (21% for the bare, and 64% for the TNT-80 sample), and (iii) equilibrium. Transfer... 

Condensation heat transfer on stainless steel tube utilizing superhydrophobic coatings was investigated. The electrophoretic deposition and spraying methods were employed to coat the tubes’ outer surface. The mixture that was synthesized for spray coating was a hybrid paint. It incorporated polyurethane matrix and a colloidal suspension containing organic nanoparticles. The hybrid paint had a proper adhesion to the substrate which caused more durability compared to the electrophoretic coating. The agglomeration of nanoparticles in the hybrid paint caused the formation of particles with larger size compared to the particles in the electrophoretic coating. Consequently, contact angle... 

Condensation heat transfer on stainless steel tube utilizing superhydrophobic coatings was investigated. The electrophoretic deposition and spraying methods were employed to coat the tubes’ outer surface. The mixture that was synthesized for spray coating was a hybrid paint. It incorporated polyurethane matrix and a colloidal suspension containing organic nanoparticles. The hybrid paint had a proper adhesion to the substrate which caused more durability compared to the electrophoretic coating. The agglomeration of nanoparticles in the hybrid paint caused the formation of particles with larger size compared to the particles in the electrophoretic coating. Consequently, contact angle... 

Abstract We report the well-controlled preparation of WS2 nanosheets-CdS nanoparticle heterojunction for photoelectrochemical (PEC) water splitting application. The WS2 nanosheets with an average thickness of ~5 nm and lateral dimensions of ~200 nm were synthesized via liquid phase exfoliation of bulk WS2 in water/ethanol solution, followed by deposition onto ITO substrate via electrophoretic method. CdS nanoparticles were grown via facile successive ion layer absorption and reaction (SILAR) method. Using these two well-controlled methods, CdS/WS2/ITO and WS2/CdS/ITO systems were fabricated. The loading of WS2 nanosheets was...