The efficient synthesis of bridged polycyclic naphthooxazocines 3 via addition of naphthalenols 1 as a bis-nucleophile to N-alkylquinolinium salts 2 is described (Scheme 1 and Table 2). This new approach provides a powerful entry into polycyclic structures containing bicyclic N,O-acetals related to bioactive compounds  

Silver nanostructures are very important agents in biomedical research, because of its unique activity against unfavorable processes in bioscience. In the current study, reagent-free facile preparation of silver nanoparticles (average diameter: 72 nm) and silver nanoparticles/ nanorods hybrid was reported via wet chemical synthesis method. Kappa-carrageenan (kC), a hydrophilic biopolymer with sulphate groups on its backbone, as capping agent was used in the reaction medium. Silver nanoparticles and silver nanoparticles/ nanorods formation was confirmed by SEM images. Further investigations were carried out using DLS data and GPC analysis  

Nanowire arrays of copper oxide were first grown vertically using simple and cost effective thermal oxidation method on a copper foil. Subsequently, in order to deposit and grow PbS nanocyrstalline thin films on CuO NWs by utilizing the chemical bath deposition technique, these arrays were immersed as the substrate in the reaction solution consisting of Pb(NO3)2, (NH2)2CS and NaOH. The final products were characterized in detail by which the formation of uniform, unique arrays of CuO@PbS core–shell NWs was confirmed. Due to the nature of methods employed in synthesis of this hetero structure, the tuning of core and shell size and consequently properties of the novel structure is easily... 

This study reports the successful fabrication of high-performance flexible binder-free lithium-ion battery anode and supercapacitor based on the synthesis of 3D hierarchical MnO2 nanoflakes (NFs) on vertically aligned carbon nanotubes (VACNTs) grown upon stainless steel (SS). The experimental results revealed that the prepared electrodes were well served as supercapacitors with a tremendous specific capacitance of MnO2 NFs VACNT/SS 1131 F/g at 0.25 A/g in 0.5 mol.L−1 Na2SO4, 518.8% more than VACNT/SS (218 F/g). Compared to other MnO2 NFs/CNT composites, as-fabricated binder-free MnO2 NFs/VACNTs electrode achieves outstanding performance with high initial discharge and charge capacities of... 

This study reports the successful fabrication of high-performance flexible binder-free lithium-ion battery anode and supercapacitor based on the synthesis of 3D hierarchical MnO2 nanoflakes (NFs) on vertically aligned carbon nanotubes (VACNTs) grown upon stainless steel (SS). The experimental results revealed that the prepared electrodes were well served as supercapacitors with a tremendous specific capacitance of MnO2 NFs VACNT/SS 1131 F/g at 0.25 A/g in 0.5 mol.L−1 Na2SO4, 518.8% more than VACNT/SS (218 F/g). Compared to other MnO2 NFs/CNT composites, as-fabricated binder-free MnO2 NFs/VACNTs electrode achieves outstanding performance with high initial discharge and charge capacities of... 

Synthesis of efficient, low-cost, and stable bifunctional electrocatalysts with earth-abundant resources for electrochemical water electrolysis is a challenging subject for large-scale energy conversion processes. Herein, we report a high-performance electrocatalyst based on vanadium oxysulfide/cobalt-cobalt sulfonitride (VOS/Co-CoSN) for oxygen and hydrogen evolution reaction (OER and HER). The Co-CoSN film was synthesized on a copper sheet (CS) by a facile electrodeposition method. Then, VOS was electrochemically grown onto the Co-CoSN@CS electrode at various deposition times. At the optimal deposition time (300 s), the obtained VOS-300/Co-CoSN catalyst was studied for OER and HER in... 

The development of electrode materials with simple preparation, favorable price, excellent electrocatalytic activity, and stability are some of the most important issues in the field of electrochemistry. Herein, we prepared Ni–Co/Ni–Co–O–P cotton flower like on a copper sheet (CS) by a convenient, efficient, and scalable electrodeposition method. The Ni–Co/Ni–Co–O–P was employed as effective binder free electrode material in two different applications such as electrocatalytic water splitting and acetaminophen (APAP) sensor. Remarkably, the Ni–Co/Ni–Co–O–P@CS exhibits low overpotentials of 310 and 90 mV at 10 mA cm−2 for oxygen and hydrogen evolution reactions in alkaline media, respectively.... 

A series of UiO-66/polyaniline (UiO-66/PANI) nanohybrids with various UiO-66 to aniline weight ratios ranging from 0.01 to 0.1 was synthesized using an in situ polymerization technique. The adsorption behavior of the neat PANI nanofiber network and the synthesized nanohybrids was examined toward anionic methyl orange (MO) dye from aqueous media. It was realized that the maximum adsorption capacity of PANI (229 mg/g) increases steadily by increasing the UiO-66 content in the nanohybrid up to 7 wt % at 426 mg/g, and then, it approximately levels off at 432 mg/g for the nanohybrid sample containing 10 wt % UiO-66, that is, UP10. Based on a thorough characterization, it was shown that UiO-66 is... 

Ag and Ni are immiscible, mainly due to their large lattice mismatch. This paper reports on their nanoscale formation of solid solution at room temperature by simple reduction reactions which lead to the amorphous Ag-Ni alloy nanoparticles (ANPs) with mono-disperse distribution. Microscopic and spectroscopic studies confirmed dependence of the alloy composition on size of nanoparticles. In the presence of different ligands such as sodium citrate, polyvinyl alcohol and potassium carbonate a mixture of silver oxide and Ag-Ni ANPs was achieved. Stoichiometry of the Ag-Ni ANPs was also found to be strongly dependent on ligands of the reduction reaction and further study shows without any ligand... 

The development of cheaper electrocatalysts for fuel cells is an important research area. This work proposes a new, simpler and low-cost approach to develop nanostructured silver electrocatalysts by using natural cellulose as a template. Silver was deposited by reduction of Ag complexes on the surface of cellulose fibers, followed by heat removal of the template to create self-standing nanostructured silver fibers (NSSFs). X-Ray diffraction (XRD) showed fcc silver phase and X-Ray photoelectron spectroscopy (XPS) demonstrated that the surface was partially oxidized. The morphology of the fibers consisted of 50 nm nanoparticles as the building blocks, and they possessed a specific surface area... 

In this research, multi-walled carbon nanotubes (MWCNTs) were modified by dendritic macromonomer. Herein, polyamidoamine with acrylamide end groups was incorporated on MWCNTs. Afterwards, poly(N-isopropylacrylamide), (PNIPAM), was grafted on polyamidoamine in a facile synthesis. Then, doxorubicin as anticancer drug was loaded on this nanocarrier. The drug release was studied at below and above the lower critical solution temperature of PNIPAM, (LCST 32 °C), 27 °C and 37 °C, respectively. At 37 °C (body temperature) the polymer shell dehydrated and the drug release increased. The profile of drug release was expressed by Higuchi's equation which indicated that the drug release mechanism was... 

Given the growing need for renewable energy and related technologies, researches have shifted to develop low-cost, stable, high-efficiency electrocatalysts in clean energy generation reactions such as water electrolysis. In the present paper, a three-dimensional Fe2TiO5/nitrogen-doped graphene (3D FTO/NG) nanocomposite is prepared using a simple, cheap and fast method, called chemical bath deposition (CBD). Structural and physical characterizations of the prepared electrocatalysts are performed by different methods such as Field Emission Scanning Electron Microscopy (FE-SEM), Energy Dispersive X-ray spectroscopy (EDX), Fourier Transform InfraRed spectra (FT-IR), Dynamic Light Scattering...