Fused Deposition Modeling with Polypropylene filament was employed to make a lap joint between Polypropylene and pre-punched Al-Mg alloy sheets, in the form of bonds between the polymeric substrate and the additive part and mechanical lock between the additive part and aluminum base sheet. Effects of the joint interface area (hole diameter of 5–13 mm) and preheating of the substrates (room temperature, 50 and 90℃) were investigated on the mechanical properties of the joints. Peak load in the tensile-shear and cross-tension tests increased with enhancement of the joint interface area (up to ˜280 N and ˜160 N, respectively). Higher joint strength in the tensile-shear test compared to the... 

Resistance spot welding was used to join austenitic stainless steel sheets. Mechanical properties of the spot welds were evaluated using tensile shear test. Mechanical behaviour was described by peak load, failure energy and failure mode. The relationship between weld fusion zone attributes and failure behaviour was studied. Generally, it was observed that increasing fusion zone size is accompanied by an increase in load carrying capacity and energy absorption capability. However, when expulsion occurs, despite almost constant weld fusion zone size, energy absorption capability reduces significantly due to increase in electrode indentation depth. Considering the failure location and failure...