Using two techniques of thermogravimetry and differential scanning calorimetry under O2 and N2 gas atmosphere from 25 to 600 °C, the thermal behavior of chromium(VI) oxide CrO3 was investigated. The identity of products at different decomposition steps was confirmed by XRD technique. Both techniques produced similar results supporting the same steps for the compound. The received products were investigated by SEM electron microscope. The form and the size of crystals were investigated. Three distinct energy changes were observed, namely, two endothermic and one exothermic in DSC. The amount of ΔH for each peak is also reported  

The compounds α-lead oxide (α-PbO) and β-lead oxide (β-PbO) were purchased from Merck co. and used for thermal investigations in laboratory. The compound was heated in a thermogravimeter at different temperature, from 25 to 400 °C. The used gas atmosphere was O2. The received products were investigated by X-ray diffraction (XRD) technique. The received product Pb3O4 was confirmed by XRD. The textures of two different morphologies of α-PbO, β-PbO and the product Pb3O4 is investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM) techniques. © 2018, Faculty of Metallurgy. All rights reserved  

The compound, alkaline lead acetate, Pb(CH3COO)2·PbO·H2O (ALA), was purchased from the Fluka Company. The X-ray diffraction film and SEM electron microgaph of this compound were obtained and reported in this paper for the first time. The thermal behavior of alkaline lead acetate (ALA) was studied using thermogravimetery (TGA) and Differential Scanning Calorimetery (DSC) techniques under an O2 gas atmosphere from 25 to 600°C. Four distinct energy changes associated with weight changes were observed, all of them being exothermic in the DSC results. The amount of ΔH for each peak is reported. © Sharif University of Technology  

In the present study, the wear behaviour of Cu-Al2O3 composites and Cu-Al alloys has been investigated. The experiment involved casting of Cu-Al alloys with 0•37, 1, 2 and 3 wt-% of aluminium under inert gas atmosphere. The composites were produced by internal oxidation of alloys at 950°C for 10 h in presence of Fe2O3 and Al 2O3 powders mixture. The microstructures of composites were studied using SEM and atomic force microscopy. To identify wear behaviour of specimens, dry sliding pin-on-disk wear tests were conducted according to ASTM G99-95a standard. The normal loads of 20, 30, and 40 N were applied on specimens during wear tests. The sliding speed and distances were selected as 0•5 m...