Pure titania porous layers consisted of anatase and rutile phases, chemically and structurally suitable for catalytic applications, were grown via micro-arc oxidation (MAO). The effect of applied voltage, process time, and electrolyte concentration on surface structure, chemical composition, and especially photocatalytic activity of the layers was investigated. SEM and AFM studies revealed that pore size and surface roughness of the layers increased with the applied voltage, and the electrolyte concentration. Moreover, the photocatalytic performance of the layers synthesized at medium applied voltages was significantly higher than that of the layers produced at other voltages. About 90% of... 

A uniformly distributed ZnO nanowire array has been grown on silicon (100) substrates by catalyst-free chemical vapor transport and condensation. The effect of growth conditions including source heating temperature, substrate temperature, and gas flow rate on growth properties of ZnO nanowire arrays are studied. Scanning electron microscopy, X-ray diffraction, and room temperature photoluminescence are employed to study the structural features and optical properties of the samples. The results show a correlation among experimental growth parameters. There is a zone for substrate temperature, by controlling gas flow rate, that uniformly distributed and well aligned ZnO nanowire arrays can be... 

In this research, the effect of applied voltage and electrolyte concentration on structure, chemical composition, optical properties, and especially photo-catalytic activity of the TiO2 layers containing micro/nano-sized pores are discussed. TiO2 layers were synthesized by micro arc oxidation (MAO) process using different electrolyte concentrations and applied voltages. Surface structure of the layers was studied by scanning electron microscope (SEM); furthermore, energy dispersive spectrophotometry (EDS), X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) techniques were employed to determine phase structure and chemical composition of the layers. Photo-activity of the...