Sharif Digital Repository

In the present work, three alumina-15 vol% zirconia composites with Y2O3, MgO as dopants and without oxide as dopant have been investigated. High energy ball milling (HEBM) provides the positive thermodynamic driving force for monoclinic to tetragonal transformation and it reduces starting temperature for the reverse martensitic transformation, meanwhile mobility of zirconium cations and oxygen anions are enhanced in zirconia by HEBM. The general, albeit heuristic, reasoning is corroborated by nanocrystallity, particle size and also the retained monoclinic seem to play an important role. After 10 h HEBM, approximately 28% zirconia tetragonal phase is achieved. Non-stoichiometric tetragonal... 

In this study, Cu-TiC nanocomposites were produced by high energy ball milling of elemental powders and in-situ formation of TiC in the copper matrix. Cu-40wt% Ti powder mixture were milled for 60 h, then graphite powder was added, subsequently milling was continued for further 10 h. Based on theoretical calculations, at this composite, the amount of TiC as reinforcement should be 60.25vol% (45.47wt%). The effect of milling time on solution progress of titanium in the copper lattice was studied by X-Ray diffraction analysis (XRD) with CuKα radiation. Considering XRD of Cu-40wt%TiC after 60 h milling data and Williamson-Hall relation, crystallite size and lattice strain of copper were... 

Two different hydroxyapatite based composites reinforced by oxide ceramic (20 wt%) nano crystals were synthesized by high-energy ball milling and sintered by pressure less technique. Alumina and titania nanoparticles as secondary phases improved densification and mechanical behavior of apatite and postponed its decomposition to the tricalcium phosphate (TCP) phases at elevated temperatures. Increasing the relative density of apatite using nano reinforcements leads to enhance the bending strength by more than 40% and 27% (as compared to the pure HA) and increase the hardness from 2.52 to 5.12 (Al2O3 composite) and 4.21 (TiO2 addition) GPa, respectively. Transmission electron microscopy (TEM),... 

The effect of high-energy ball milling on the textural evolution of alumina nanopowders (compaction response, sinter-ability, grain growth and the degree of agglomeration) during post sintering process is studied. The applied pressure required for the breakage of the agglomerates (P y) during milling was estimated and the key elements of compressibility (i.e. critical pressure (P cr) and compressibility (b)) were calculated. Based on the results, the fracture point of the agglomerates decreased from 150 to 75 MPa with prolonged milling time from 3 to 60 min. Furthermore, the powders were formed by different shaping methods such as cold isostatic press (CIP) and uniaxial press (UP) to better... 

Compressibility of a nanostructured Al-5AlN composite powder synthesised via high energy ball milling for various times was studied by means of a modified Heckel equation. Since workhardening and morphological changes take place by milling evolution, the compressibility was consequently affected. Strengthening of composite compacts was influenced by milling and compaction processes, i.e. strength of compacts increased at longer milling times and higher compaction pressures. It was found that, at the initial stages of milling and higher compaction pressures, the strengthening was mostly affected from compaction process, whereas the milling strengthening fraction was near to unity at lower... 

High strength Al-AlN composites were synthesized via high-energy milling and sintering technique. Al-X wt.% AlN (X = 0, 2.5, 5 and 10) composite powders were milled in a planetary ball mill for 25 h. Morphology, particle size distribution, crystallite size, micro-strain, and microhardness of milled powders were studied. Ball-milled powders were degassed at 400 °C for 30 min. After uniaxial cold compaction, composite compacts were sintered at 650 °C for 20, 30 and 60 min under N2 atmosphere. Effects of reinforcement content, degassing treatment and sintering time on the sinterability of powders were investigated. The results revealed that the sinterability was degraded by increasing the... 

W-20 wt.% Cu powder mixture was mechanically alloyed by high-energy ball milling for various times and the effect of mechanical alloying (MA) on the sintering response of the composite compacts was investigated. The densification, microstructure, hardness and electrical conductivity after solid phase sintering (SPS) and liquid phase sintering (LPS) were examined. It was shown that the microstructure of mechanically alloyed powder profoundly influence the sintering response, i.e. a meaningful relationship between the sintering kinetics and the milling time was observed. It is suggested that MA disintegrates the W-W particle networks and increases the contribution of solid phase sintering...