A heterogeneous tungstate-based catalyst has been prepared for selective oxidation of sulfides to sulfoxides in the presence of 30% H2O2. The catalyst was prepared via immobilization of high amounts of WO4 2− onto the cross-linked poly(ammonium ethyl acrylamide) coated magnetic nanoparticles (MNP). FT-IR, TEM, TGA, VSM, XRD, EDX, and CHN analysis were used for characterization of catalyst. Variety of sulfides successfully converted to the related sulfoxides using 1 mol% of catalyst at room temperature in high yields. The catalyst was easily recovered and reused up to 6 times without loss of activity  

In this work, a novel heterogeneous organocatalyst was synthesized by immobilization of hydroxide ions on the modified salep as a natural polymer. Because of the grafting of ionic polymer chains onto the salep backbone, catalyst has high loading level of hydroxide ions (3.01 mmol/g). The resulting catalyst shows excellent activity in the synthesis of 4H-benzo[b]pyrans in water at room temperature in short reaction times. The present catalyst and protocol represent a simple, ecologically safe and cost-effective route to synthesize 4H-benzo[b]pyrans with high product yield, as well as easy catalyst recycling