Sharif Digital Repository

Hydroxyapatite (HA) coatings in and onto anodized TiO2 nanotube arrays were presented and prepared by electrophoretic deposition technique (EPD). Coatings were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). EPD proved to be an innovative and versatile technique to coat HA on and into nanotubular structures of TiO2 with enhanced adhesion between nanotubes and HA particles provided by mechanical interlocking. After EPD of HA on TiO2 layer, samples were sintered at 400 °C, 600 °C and 800 °C for 2 h in an Ar atmosphere. Effect of EPD processing parameters on thickness of the deposits and rate of deposition was elucidated for HA coatings on the nanotubular TiO2... 

The effect of grit blasting parameters on the surface roughness of Ti-6Al-4V alloy as the substrate for plasma-sprayed hydroxyapatite (HA) coatings was examined using the factorial and Taguchi designs of experiments. In this study, two grit materials (Al2O3 and SiO2) each at two sizes, and two types of blasting systems (pressure and suction) were used. An equivalent surface roughness of 3.51 μm was obtained in three optimum conditions. The results of the Taguchi designed experiments were analyzed using signal to noise ratio. The tensile bonding strength of HA coatings deposited on the roughened substrates at the three different optimum conditions was measured by the standard adhesion test... 

Micro Arc Oxidation (MAO) process was utilized to fabricate nano bioceramic TiO 2-hydroxyapatite coatings on titanium substrates. Samples were produced in electrolytes contained 1 g/l β-glycerophosphate and 5, 10 and 15 g/l calcium acetate for 3, 6 and 10 min at 350 V. The techniques including XRD, XPS, SEM, FESEM and EDX were employed to study the effect of processing parameters. Hydroxyapatite, anatase, α-tri calcium phosphate and calcium titanate phases as well as 30-60 nm-size crystals were detected in the coating layer. It was also observed that the pore volume would increase by increasing the electrolyte concentration. The growth time was also found to influence the total pore volume.... 

The low erosion resistance of titanium and its alloys has prevented their widespread application as joint implants. In addition, one essential requirement for the implants to bond with the living bone is the formation of a bone-like apatite on their surfaces in the host body. To enhance the erosion resistance of the surface, a diffused layer of TiB2 was formed at 1000uC on the commercial pure titanium. Hydroxyapatite was then coated on the boronised titanium by means of dip coating in a sol-gel solution. In order to confirm the biocompatibility of the specimens, they were soaked in a simulated body fluid for several days. The surface morphology of the specimens after exposure was studied by... 

Biocompatible nanostructured coating plays an important role in enhancement of osseointegration ability of metallic implants. This study sets out to obtain optimized SiC concentration in Hydroxyapatite (HA) coating on AISI 316L stainless steel alloy through electrophoretic deposition method. Effect of SiC concentrations (1, 2, and 3%.wt) on the morphology, corrosion behaviour, and mechanical properties of the HA coating is investigated. Results show that SiC could obstruct the formation and growth of micro cracks in the HA coating where HA-3%SiC is considered as a crack free coating. Electrochemical tests reveal that SiC has improved the corrosion resistance of HA coating, and HA-3%SiC... 

To improve the biocompatibility and corrosion resistance of 316L SS (Stainless Steel) metal implants, HAp(hydroxyapatite)/TiO2/Al2O3 nanocomposite coating was created using dip sol-gel method sintered at 550 °C. The weight percentage of TiO2+ Al2O3 in these coatings was 20, 30, and 40% wt. In this study, characterization was performed using FTIR (Fourier-Transform Infrared Spectroscopy), XRD, FE-SEM (Field Emission Scanning Electron Microscope), EDS (Energy Dispersive Spectroscopy), DLS (Dynamic Light Scattering), Pull-off, and AFM (Atomic Force Microscopy) analysis. The potentiodynamic polarization and EIS (Electrochemical Impedance Spectroscopy) were performed in the simulated body fluid... 

To improve the biocompatibility and corrosion resistance of 316L SS (Stainless Steel) metal implants, HAp(hydroxyapatite)/TiO2/Al2O3 nanocomposite coating was created using dip sol-gel method sintered at 550 °C. The weight percentage of TiO2+ Al2O3 in these coatings was 20, 30, and 40% wt. In this study, characterization was performed using FTIR (Fourier-Transform Infrared Spectroscopy), XRD, FE-SEM (Field Emission Scanning Electron Microscope), EDS (Energy Dispersive Spectroscopy), DLS (Dynamic Light Scattering), Pull-off, and AFM (Atomic Force Microscopy) analysis. The potentiodynamic polarization and EIS (Electrochemical Impedance Spectroscopy) were performed in the simulated body fluid... 

To improve the biocompatibility and corrosion resistance of 316L SS (Stainless Steel) metal implants, HAp(hydroxyapatite)/TiO2/Al2O3 nanocomposite coating was created using dip sol-gel method sintered at 550 °C. The weight percentage of TiO2+ Al2O3 in these coatings was 20, 30, and 40% wt. In this study, characterization was performed using FTIR (Fourier-Transform Infrared Spectroscopy), XRD, FE-SEM (Field Emission Scanning Electron Microscope), EDS (Energy Dispersive Spectroscopy), DLS (Dynamic Light Scattering), Pull-off, and AFM (Atomic Force Microscopy) analysis. The potentiodynamic polarization and EIS (Electrochemical Impedance Spectroscopy) were performed in the simulated body fluid... 

The most common reasons for hard-tissue implant failure are structural loosening and prosthetic infections. Hence, in this study, to overcome the first problem, different bioinspired coatings, including dual acid-etched, anodic TiO2 nanotubes array, anodic hierarchical titanium oxide (HO), micro- and nanostructured hydroxyapatite (HA) layers, and HA/chitosan (HA/CS) nanocomposite, were applied to the titanium alloy surfaces. X-ray diffraction and FTIR analysis demonstrated that the in situ HA/CS nanocomposite formed successfully. The MTT assay showed that all samples had excellent cell viability, with cell proliferation rates ranging from 120% to 150% after 10 days. The HO coating...