Simple compression and microscopy techniques were employed to characterise the microstructural origin of the deformation behaviour of nickel base superalloy IN625 during large strain testing. The alloy exhibited a four-stage strain hardening response similar to that previously reported for low stacking fault energy face centred cubic alloys. At strains lower than about -0.06 (stage A), a falling regime of the hardening rate was observed. This stage was followed by a second stage (stage B) of slow increasing hardening rate, which was found to be coincident with the formation of Lomer-Cottrell locks. The second falling regime of strain hardening (stage C) was seen in the strain range of -0.25...