In an attempt to reduce the oxidation and Cr evaporation rates, various protective coating layers with a nominal composition of NiCo 2-xFexO4 (x = 0, 0.5, 1) were deposited on the SUS 430 ferritic stainless steel substrate, as interconnect for solid oxide fuel cell application, by sol-gel dip coating method. Then, the coated samples were soaked at 750 C for 2.5 h in N2 and subsequently for 2.5 h in air. Phase composition and microstructure of the coatings were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Moreover, long-term isothermal oxidation experiment and area specific resistance (ASR) measurement were also carried out on the coated samples. Results... 

Lanthanum chromite coating occupies a noticeable position as a ceramic coating on metallic interconnects in solid oxide fuel cells because of its excellent electrical conductivity, high oxidation resistance and desirable chemical stability in both oxidizing and reducing atmospheres. In the present work, a sol-gel process based on the dip-coating technique was used to prepare dense and uniform coatings on metallic alloy for interconnect application (AISI 430 type). The effect of strontium and calcium doping into lanthanum chromite structure on electrical conductivity and oxidation behavior of the coated sample has been investigated. The oxidation behavior was evaluated by cyclic oxidation... 

Abstract: The effect of de-siliconization on the oxidation behavior of AISI 430 stainless steel used for solid oxide fuel cell interconnect application was investigated. De-siliconization treatment was conducted via heating steel parts in an H2 environment. The de-siliconized substrates were then coated with a Mn1.5Co1.5O4 spinel coating, using wet spray method. For comparison, a similar coating process was applied on the as-received AISI 430 stainless steel specimens. Oxidation kinetics of coated interconnects were evaluated at 700, 800 and 900 °C in air. Results showed that the de-siliconization surface treatment decreased oxidation rates, with kinetic rates (g2 cm−4 s−1) of 4.39 × 10−14... 

Mn1.5Co1.5O4 oxide spinels are widely used as protective coatings for stainless steel interconnects within planar solid oxide fuel cell stacks. Containing both cubic and tetragonal crystalline phases, these Mn/Co oxide spinels exhibit favorable thermal stability and electronic conductivity for the SOFC interconnect application. Slurry-based coating applications of Mn/Co oxides require precursor powders, which can benefit from being nano-structured. In this study, the sol-gel synthesis of nanocrystalline Mn1.5Co1.5O4 spinel is investigated. The decomposition of sol-gel precursors, as well as the crystalline phase structures and microstructures of the product Mn1.5Co1.5O4 are characterized by...