Smart Coating Incorporated with Inhibitor-Enclosed Nanocontainers for Corrosion Protection of Steel
, Ph.D. Dissertation Sharif University of Technology ; Ghorbani, Mohammad (Supervisor)
Abstract
In this thesis a smart anticorrosive pH-responsive coat was developed with layer by layer (LbL) technique in the assembly of SiO2/CTAB/PSS/HMTA/PSS/PEI/PSS. SiO2 nanoparticles were prepared from Matland Company (Iran) with average size of 24 nm. At first, the corrosion inhibition of HMTA for API 5L Grade B steel in 3.5 wt.% NaCl solution was investigated. Tafel polarization technique showed the optimum concentration of HMTA was 0.08 M with 92% corrosion inhibition efficiency as the morphology of coverage and adsorption on the steel surface was confirmed by SEM and EDS. AFM results showed the roughness of the surface decreased from 241 nm to 56 nm that is attributed to HMTA adsorption on the...