4340 steel bars were austenitized at 850°C for 1 hour followed by heating at 700°C (ferrite and austenite region) for 90 min and quenching into a salt bath with different temperatures of 300, 350, 400 and 450°C. The steel bars were held for 1 hour at these temperatures before air cooling to room temperature. Various ferrite-bainite microstructures with 34% volume fraction of ferrite and different bainite morphologies were obtained. The results of SEM studies showed that by increasing the austempering temperature, the morphology of bainite varies from lower to upper bainite. According to the T-T-T diagram of the studied steel, the bainite transformation will not complete for the holding time... 

4340 steel bars were austenitized at 850 °C for 1 h followed by heating at 700 °C for 90 min and quenching into a salt bath at the temperature range of 300-450 °C for 1 h to obtain dual structures with 34 vol.% fraction ferrite and various bainite morphologies. SEM studies showed that by increasing the austempering temperature, bainite morphology varies from lower to upper bainite. Tensile, impact and hardness tests revealed that increasing the austempering temperature from 300 to 400 °C leads to a reduction in yield and ultimate tensile strength, hardness, uniform and total elongation and impact energy. But in dual phase steel produced by austempering at 450 °C, yield and tensile strength...