The fabrication of supported noble metal nanocrystals (NCs) with well-controlled morphologies have been attracted considerable interests due to their merits in a wide variety of applications. Photodeposition is a facile and effective method to load metals over semiconductors in a simple slurry reactor under irradiation. By optimizing the photodeposition process, the size, chemical states, and the geometrical distribution of metal NCs have been successfully tuned. However, metal NCs with well-controlled shapes through the photodeposition process have not been reported until now. Here, we report our important advances in the controlled photodeposition process to load regular noble metal NCs.... 

TiO2, transition metal (Cr, Mn, Fe, Co, Ni, Cu, and Zn)- and aluminum-doped TiO2 nanoparticles were prepared by the sol-gel technique. The sulfated catalysts were prepared by the impregnation method with H2SO4 solution. The catalysts were characterised by X-ray diffraction (XRD), BET surface area measurement, diffuse reflectance spectroscopy (DRS), and Fourier transform infrared (FTIR) techniques. The sulfate content of the metal-incorporated samples was considerably higher than for SO4 2-/TiO2. The metal doping brought about a considerable reduction in the extent of sulfate loss from the catalyst surface due to the wide dispersion on the surface. The SO4 2-/TiO2 and SO4 2-/M/TiO2... 

A systematic comparison of single and binary metal oxide T1O2, TiO2-Ga2O3, TiO2-Er 2O3 and TiO2-Ta2O5 gas sensors with nanocrystalline and mesoporous microstructure, prepared by sol-gel route, was conducted. The gas sensitivity was increased by secondary phase introduction into TiO2 film via two mechanisms, firstly through the inhibition of anatase-to-rutile transformation, since the anatase phase accommodates larger amounts of adsorbed oxygen, and secondly through the retardation of grain growth, since the higher surface area provides more active sites for gas molecule adsorption. The binary metal oxides exhibited a remarkable response towards low concentrations of CO and NO2 gases at low...