Sharif Digital Repository

By fabrication of several bolometric detectors on the YBCO film made of Metal-Organic Deposition (MOD) and the effect of pattering and film parameters on the optical responsivity of transition edge sensors is investigated. The low cost nonfluorine (MOD) method has been applied to fabricate YBCO thin films with different patterning parameters. The measurement results of the optical responsivity versus modulation frequency up to 100 KHz for these devices are reported  

The effect on the thermal parameters of superconducting transition-edge bolometers produced on a single crystalline SrTiO3 (STO) substrate with and without a CeO2 buffer layer was investigated. Metal-organic deposition was used to deposit the 20-nm CeO2 buffer layer, whereas RF magnetron sputtering was applied to fabricate 150-nm-thick superconducting YBa2Cu3O7-δ (YBCO) thin film. The critical transition temperature for both of the YBCO films was 90 K, and the transition width was ∼1.9 K. The bolometers fabricated from these samples were characterized with respect to the voltage phase and amplitude responses, and the results were compared with that of simulations conducted by applying a... 

We present the results of a bolometric transition-edge sensor made of a high-Tc superconductor YBCO thin film prepared by fluorine-free metal-organic deposition. The structure of the films was characterized by X-ray diffraction and scanning electron microscopy, and the superconducting properties were determined by R-T measurements. The applicability of the resulting film as an infrared sensor is reported here. The optical response in the range of near infrared and the noise characteristics of the patterned bolometer are measured and analyzed. The dependence of device sensitivity on the bias current and modulation frequency is also investigated. As it is presented in this paper, the results... 

We report on the response of a monolithic high Tc transition-edge bolometer to about 3 mmWave for the first time. The detector structure consisting of 400-nm YBa2Cu3O7-x(YBCO) film on buffered yttria stabilized zirconia substrate without any coupled antenna, shows bolometric type responsivity to the 3-mmWave radiation at its transition temperature. The YBCO thin film Ce0.9La0.1O2 buffer layer are both fabricated by the metal-organic deposition method. The meander line pattern of the bolometer is designed for obtaining maximum absorption and responsivity possible when the polarized radiation of the source is aligned with the pattern. Meander lines are 50 micrometers wide and 1.5-mm long. We... 

We report on the results of a YBa2Cu3O7−x (YBCO) superconductive transition edge bolometer (TEB) fabricated on a Ce0.9La0.1O2−7 (CLO) buffered single crystalline yttria-stabilized zirconia (YSZ) substrate. Metal organic deposition was used for the fabrication of both the YBCO thin film as well as CLO buffer layer, while standard photolithography was applied for TEB preparation. YBCO thin film properties were analysed using scanning electron microscopy (SEM), X-ray diffraction (XRD), AC susceptibility and resistance versus temperature measurements. Optical response of the TEB in terms of voltage amplitude and phase was analysed and measured through four-probe technique in a liquid nitrogen... 

We report on the results of a YBa2Cu3O7−x (YBCO) superconductive transition edge bolometer (TEB) fabricated on a Ce0.9La0.1O2−7 (CLO) buffered single crystalline yttria-stabilized zirconia (YSZ) substrate. Metal organic deposition was used for the fabrication of both the YBCO thin film as well as CLO buffer layer, while standard photolithography was applied for TEB preparation. YBCO thin film properties were analysed using scanning electron microscopy (SEM), X-ray diffraction (XRD), AC susceptibility and resistance versus temperature measurements. Optical response of the TEB in terms of voltage amplitude and phase was analysed and measured through four-probe technique in a liquid nitrogen...