The effect of SiO2/Al2O3 ratio on high silica content nano-sized HZSM-5 stability and selectivity in conversion of methanol to propylene (MTP) has been investigated in a continuous flow isotherm fixed-bed reactor. Highly crystalline HZSM-5 zeolite samples with SiO2/Al2O3 ratios ranging 150–200 have been prepared and characterized using XRD, ICP-AES analytical techniques, NH3-TPD, BET surface area and SEM imaging for studying their physical and chemical behavior. The reaction was conducted at 480 °C and 1bar with WHSV = 1 h−1 and a solution with 1:1 wt% of methanol and water as feed. Over thoroughly monitoring the catalyst synthesis conditions, the nanocrystal ZSM-5 zeolite samples were... 

In this paper, the effects of two methods of iridium impregnation into HZSM-5 on catalyst stability, selectivity for propylene and byproducts in the conversion of methanol to propylene (MTP) were investigated in a continuous flow isotherm fixed-bed reactor. XRD, BET surface area, NH 3-TPD and ICP-AES analytical techniques were applied to define the physical and chemical characteristics of zeolites. The reaction was conducted at 480°C and 1 bar with WHSV = 1 h -1, and with an equal weight percent of methanol and water in the feed. The results revealed that iridium impregnation into HZSM-5 powder led to enhanced propylene selectivity (8%) and catalyst stability while iridium impregnation into... 

The effect of particle size on the catalytic activity of H-ZSM-5 zeolite in the methanol to propylene (MTP) reaction was investigated in a fixed-bed flow reactor under the operating conditions of T = 460 °C, P = 1 atm, and WHSV = 1 h-1. Nano and micro size H-ZSM-5 were prepared by reflux and hydrothermal crystallization methods, respectively. The nano and micro H-ZSM-5 were characterized using XRD, NH3-TPD, BET area, SEM and ICP-AES analytical techniques. Nano size H-ZSM-5 showed higher activity and stability compared to the micro size H-ZSM-5. Nano H-ZSM-5 was also found to have higher selectivity to propylene than the micro size H-ZSM-5. © 2009 Elsevier B.V. All rights reserved