The adhesion of hydroxyapatite (HA) as a coating for the AZ91 magnesium alloy substrate can be improved by using the sputtering method and an intermediate layer, such as ZrN. In this study, HA coatings were applied on ZrN intermediate layers at a temperature of 300 °C for 180, 240, 300, 360, and 420 min by ion beam sputtering. A profilometer device was used to study the HA coating thickness, which changed from 2 μm for the 180-min deposition to 4.7 μm for 420-min deposition. The grazing incidence X-ray diffraction analysis method and the Williamson–Hall analysis were used for structural investigation. As the deposition time increased, the crystalline size increased from 50 nm to 690 nm.... 

High strength Al-AlN composites were synthesized via high-energy milling and sintering technique. Al-X wt.% AlN (X = 0, 2.5, 5 and 10) composite powders were milled in a planetary ball mill for 25 h. Morphology, particle size distribution, crystallite size, micro-strain, and microhardness of milled powders were studied. Ball-milled powders were degassed at 400 °C for 30 min. After uniaxial cold compaction, composite compacts were sintered at 650 °C for 20, 30 and 60 min under N2 atmosphere. Effects of reinforcement content, degassing treatment and sintering time on the sinterability of powders were investigated. The results revealed that the sinterability was degraded by increasing the...