A hydrogen-selective nano-composite ceramic membrane was prepared by depositing a dense layer composed of SiO2 and Al2O 3 on top of a graded multilayer substrate using co-current chemical vapor deposition (CVD) method. The multilayer substrate was made by dip-coating a macroporous α-alumina tubular support by a series of boehmite solutions to get a graded structure. Using DLS analysis, it was concluded that decreasing hydrolysis time and increasing acid concentration lead to smaller particle size of boehmite sols. XRD analysis was carried out to investigate the structure of intermediate layer and an optimized calcination temperature of 973 K was obtained. SEM images indicated the formation... 

Tubular ceramic membranes were synthesized by depositing a dense layer of silica-alumina on top of a multilayer substrate using co-current chemical vapor deposition (CVD) method. The multilayer substrate was prepared by coating with a series of bohemite sols with certain particle sizes. Cross-sectional and surface images obtained from high resolution FESEM showed that the intermediate layer had a thickness of about 1μm and the top selective layer was uniform and dense with a thickness of less than 100nm. Permeance tests, which were carried out with H 2, CO 2, N 2 and CH 4 at a high temperature range of 923-1073K, indicated that gas permeation took place via different mechanisms through...