Graphene oxide (GO) sheets were synthesized through a modified Hummers' method. Using high resolution transmission electron microscopy the thickness of the GO sheets in a multilayer structure of stacked GO sheets was found ∼0.8 nm. A nanosecond pulsed laser (with wavelength of 532 nm and average power of 0.3 W) was applied for effective and environment friendly reduction of the GO sheets in an ammonia solution (pH ∼9) at room temperature conditions. The deoxygenation of the GO sheets by the pulsed laser reduction method was confirmed by using UV-visible, Fourier transform infrared, X-ray photoelectron spectroscopy (XPS) and thermo gravimetric analysis. Based on XPS analysis, the O/C ratio of... 

Laser ablation of titanium target in distilled water for synthesis of colloidal nanoparticles is studied both experimentally and theoretically. The effects of laser parameters such as wavelength, pulse energy, fluence and shot numbers on the ablation rate and size properties of colloidal nanoparticles are investigated. The experimental approach addresses the interesting issue for finding the optimal main experimental parameters of laser ablation. The theoretical thermal model of nanosecond pulsed laser ablation is developed to visualize the evolution of temperature distributions and ablation depth. The simulation result of ablation depth has been compared with the experimental result... 

Optothermal properties of noble metal nanoparticles can be used in a wide range of applications. This paper presents the results of a theoretical study on the utilization of laser-induced heating of a gold nanoparticle (GNP) to melt a region of a transparent material with sub-wavelength spatial resolution. The considered system consists of a 10 or 15nm diameter GNP fixed inside a silica substrate. The silica surface is covered with a thick film of the transparent polymeric or crystalline material. The heating and melting processes are studied under a 7.5ns pulsed laser illumination. Calculations are conducted under three temperature limits, on the maximum temperature of the free electrons,... 

Nanosecond lasers of different intensities were pulsed into sputter-deposited amorphous thin films of near equiatomic Ni/Ti composition to produce partially crystallized highly sensitive R-phase spots surrounded by amorphous regions. Scanning electron microscopy having secondary and back-scattered electrons, field emission scanning electron microscopy, optical microscopy and X-ray diffraction patterns were used to characterize the laser treated spots. Effect of nanosecond pulse lasering on microstructure, morphology, thermal diffusion and inclusion formation was investigated. Increasing beam intensity and laser pulse-number promoted amorphous to R-phase transition. Lowering duration of the...