Sharif Digital Repository

In this research, three fibers including cellulose acetate (CA), CA–phenyltriethoxysilane (PTES) prepared via sol–gel electrospinning and sol–gel–based CA fibers immersed in PTES solution (dipped–CA–PTES) were prepared. The composition and morphology of the prepared fibers were evaluated by energy dispersive X-ray spectroscopy and field emission scanning electron microscopy. The prepared fibers were implemented in a home–made needle trap device, followed by thermal desorption of the selected chlorobenzenes (CBs) to a gas chromatography–flame ionization detector. Finally, parameters affecting the extraction methodology such as the amount of sorbent, extraction time and temperature, desorption... 

Three-dimensional (3D) polyamide scaffolds were fabricated by applying a solvent bath as the collecting element. Electrospun nanofibers were immersed into the solvent bath to give a material with a laminated 3D texture. In parallel, 2D nanofibers were synthesized and utilized as microextractive phases in a needle trap device to compare the capabilities of 2D and 3D materials in terms of headspace extraction of various chlorobenzenes (chlorobenzene, 1,2-dichlorobenzene, 1,4-dichlorobenzene, 1,2,4-trichlorobenzene and 1,2,3,4-tetrachlorobenzene). The results demonstrate the superiority of 3D nanofibrous scaffolds over 2D mats. The porosity, morphology, and thermal stability of the 3D scaffolds... 

A superhydrophobic extractive phase was prepared and packed in a needle trap microextraction device for extraction of volatile organic compounds, followed by their determination by gas chromatography. The superhydrophobic phase was prepared by surface modification of melamine formaldehyde (MF) sponge embedded by reduced graphene oxide (rGO). The overall properties of the modified MF along with its high sorption capacity and low cost fabrication were indicative of its feasibility to be highly suitable for extraction of organic pollutants. The determined water contact angle (>150o) from the surface of melamine formaldehyde–reduced graphene oxide (MF–rGO) revealed its high affinity toward... 

The authors have synthesized a superhydrophobic silica aerogel by using a sol-gel technique. The material is shown to be an efficient sorbent for needle trap microextraction of chlorobenzenes. Hydrophobicity affects the performance of the sorbent as shown by altering the ratio between tetraethylorthosilicate (TEOS) and methyltrimethoxysilane when synthesizing the sorbent. The observed contact angle (which is >150°) underpins the superhydrophobic properties of the aerogel. The microstructure of the sorbent was investigated by BET adsorption, revealing a surface area above 1000 m2 g−1. The sorbent was applied to needle trap extraction of chlorobenzenes from aqueous samples, and their... 

Superhydrophobic materials have attracted many attentions in recent years while their application in sample preparation remained almost intact. In this project, a rough surface of melamine formaldehyde foam was silanized by chemical deposition of trichloromethylsilane to form a highly porous and superhydrophobic material, presumably a suitable medium for extracting non–polar compounds such as benzene and its methyl derivatives. The prepared sorbent was packed in a needle for the headspace needle–trap microextraction of benzene, toluene, ethylbenzene and xylenes (BTEX). Major parameters associated with the extraction/desorption processes were considered for optimization. Under the optimized...