In this study, electrolytic plasma processing (EPP) was employed for surface nitrocarburizing of AISI 1020 steel in a urea electrolyte, where the substrate samples were connected cathodically to a high-voltage DC current power supply. The structural, mechanical, wear and corrosion properties of the samples treated for 3-5 min were investigated. The results show that the surface layers formed on the samples by this treatment at 220 V have a ferritic nitrocarburizing characteristic which consists of a compound layer and diffusion zone. The surface layers of the treated samples at 240 V consisted of a compound layer, martensitic layer and diffusion zone, respectively, which is a marker of... 

The effects of nitriding, nitrocarburizing and shot peening on fatigue behavior of AISI D3 cold work tool steel were investigated. Five batches of fatigue specimens were manufactured according to the ASTM E466-96 standard. All specimens were quenched and tempered to a hardness of 50 HRC. One group of specimens was shot peened with an Almen intensity of 16 A, one group was nitrocarburized, one group was gas nitrided by single stage and another group was also nitrided by double stages. Rotating-bending fatigue tests were carried out. Our results showed that nitriding and nitrocarburizing treatments did not have a beneficial effect on the fatigue resistance of D3 tool steel. Fatigue test...