Sharif Digital Repository

In this research, microstructure and corrosion properties of plasma nitriding and post-oxidation treated AISI 316 austenitic stainless steel have been studied. The plasma nitriding treatment was carried out at 450 C for 5 h in a D.C. plasma setup with a gas mixture of 25% N2-75% H2 followed by post-oxidation in gas mixtures of O2/H2: 1/3, 1/5, 1/9 and 1/12 for 30 min. The treated samples were characterized by SEM, XRD and roughness testing. Potentiodynamic and cyclic polarization tests were also employed to evaluate the corrosion resistance of the samples. The results showed that plasma nitriding treatment decreases corrosion resistance of the steel substrate. However, post-oxidizing... 

In this work, the silver particle absorption and antibacterial activity of cotton fabric when modified by low temperature plasma were investigated. The modification consisted of plasma pre-functionalization followed by one-step wet treatment with silver nitrate solution. Oxygen and nitrogen were used as the working gases in the system, and the results were compared. The results showed that nitrogen plasma-treated samples can absorb more silver particles than oxygen-treated samples, and thus the antibacterial activity of the samples in this case, which was analyzed by the counting bacteria test, was increased considerably  

This study involves the capability of severe shot peening (SSP) as a catalyst intake for plasma nitriding process and the probability of reducing the requirement of thermal energy individually on the diffusion of interstitial atoms. To this end, combination of mechanical-thermal energy is run with pure thermal plasma assisted energy. Therefore, SSP is exposed to AISI 304 austenitic stainless steel as a former treatment and gradient structured surface (nanograined zone, ultrafine grain martensite-twin intersections zone and twin densed zone) is created. Then, plasma nitriding at 400 0 C-4h and 475 0 C-2h temperature-duration conditions. The condition of 475 0 C-2h provides the requirements of... 

On silicon substrates, boron nitride nanosheets (BNNS) consisting of interconnected hexagonal boron nitride nano-layers were produced via chemical vapor deposition process at 1200 °C whose roughness's are at the micrometer- and nanometer-scale. The BNNS were functionalized in argon plasma admixed with ammonia or nitrogen or oxygen. The samples were characterized to investigate the surface chemistry and structural changes after plasma treatment using X-ray photoelectron spectroscope and Micro-Raman spectroscope techniques, respectively. While no significant changes in the surface features, upon plasma treatments of the BNNS, were noticed during SEM and TEM examination, the oxygen functional... 

In this study, the fatigue behavior of Ti-6Al-4V alloy is tend to be improved by severe plastic deformation via shot peening and plasma nitriding. Shot peening with sub-branches: Conventional shot peening (A12-14), severe shot peening (A28–30 and A34-36) and repeening (N6-8) are exposed. Besides plasma nitriding is implemented at 500 °C, 550 °C and 600 °C with the durations of 4, 8 and 16 h. Due to utilization of shot peening as prior severe plastic deformation during diffusion of nitrogen, two methods are applied in sequence. Severe shot peening forms ultra-fine crystals and oriented grains by disintegrating of α and β phases just below the surface and increases surface roughness. Plasma... 

The comparative study of Active Screen Plasma Nitriding (ASPN) treatment of two Finemet-type alloys with the compositions of Fe73.5Si 13.5B9Nb3Cu1 and Fe 77Si11B9Nb2.4Cu0.6 was investigated in different temperatures ranging from 410°C to 56°C. Differential Scanning Calorimetry (DSC), X-Ray Diffractometery (XRD), Atomic Force Microscopy (AFM), Scanning Electron Microscopy (SEM), electrical resistivity, microhardness measurements and magnetic characterization by a Vibrating Sample Magnetometer (VSM) were utilized to characterize the treated samples. The comparison of the DSC data for the alloys suggested that the smaller amount of Nb as a growth inhibitor shifted the crystallization...