Sharif Digital Repository

The low temperature perovskite-type strontium titanate (SrTiO 3) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route. The prepared sol had a narrow particle size distribution with hydrodynamic diameter of about 17 nm. X-ray diffraction (XRD) revealed that the synthesized powders had a perovskite-SrTiO 3 structure with preferable orientation growth along the (1 0 0) direction. TEM images showed that the average crystallite size of the powders annealed in the range 300-800°C was around 8 nm. FE-SEM analysis and AFM images revealed that the deposited thin films had mesoporous and nanocrystalline structure with the... 

Magnetite (Fe3O4) nanostructures with different morphologies including uniform nanoparticles, magnetic beads and nanorods were synthesized via a co-precipitation method. The synthesis process was performed at various temperatures in the presence of polyvinyl alcohol (PVA) at different concentrations. It is shown that small amounts of PVA act as a template in hot water (70 °C), leading to the oriented growth of Fe3O4 nanorods, which was confirmed by selected area electron diffraction. Individually coated magnetite nanoparticles and magnetic beads were formed at a relatively lower temperature of 30 °C in the folded polymer molecules due to the thermo-physical properties of PVA. When a moderate... 

Perovskite-type barium strontium titanate (BST) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route at room temperature. The prepared sol had a narrow particle size distribution of about 20 nm. X-ray diffraction (XRD) revealed that phase composition and preferable orientation growth of BST depended upon the annealing temperature. Transmission electron microscope (TEM) images showed that the crystallite size of the powders decreased with increasing annealing temperature from 8 nm at 25 °C down to 5 nm at 800 °C. Field emission scanning electron microscope (FE-SEM) analysis and atomic force microscope (AFM) images... 

Nanocrystalline nickel titanate (NiTiO3) thin films and powders with mesoporous structure were produced at the low temperature of 500 °C by a straightforward particulate sol-gel route. The sols were prepared in various Ni:Ti molar ratios. X-ray diffraction and Fourier transform infrared spectroscopy revealed that the powders contained mixtures of the NiTiO 3 and NiO phases, as well as the anatase-TiO2 and the rutile-TiO2 depending on the annealing temperature and Ni:Ti molar ratio. Moreover, it was found that Ni:Ti molar ratio influences the preferable orientation growth of the nickel titanate, being on (202) planes for the nickel dominant powders (Ni:Ti ≥ 75:25) and on (104) planes for the... 

Low temperature lithium titanate compounds (i.e., Li4Ti 5O12 and Li2TiO3) with nanocrystalline and mesoporous structure were prepared by a straightforward aqueous particulate sol-gel route. The effect of Li:Ti molar ratio was studied on crystallisation behaviour of lithium titanates. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders were crystallised at the low temperature of 500 °C and the short annealing time of 1 h. Moreover, it was found that Li:Ti molar ratio and annealing temperature influence the preferable orientation growth of the lithium titanate compounds. Transmission electron microscope (TEM) images showed that the average... 

Nanocrystalline zinc titanate (ZnTiO3) thin films and powders with purity of 94% were produced at the low sintering temperature of 500 °C and the short sintering time of 1 h by a straightforward aqueous particulate sol-gel route. The effect of Zn:Ti molar ratio was studied on the crystallisation behaviour of zinc titanates. The prepared sols showed a narrow particle size distribution in the range 17-19 nm. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders contained mixtures of the rhombohedral-ZnTiO3, cubic-ZnO, cubic-Zn2TiO4 phases, as well as the anatase-TiO2 and the rutile-TiO2 depending on the sintering temperature and Zn:Ti molar ratio.... 

Nanocrystalline neodymium titanium oxide thin films and powders with different phase compositions with mesoporous structure were produced by a straightforward particulate sol-gel route. The sols were prepared in various Nd:Ti molar ratios and they showed a narrow particle size distribution in the range 20-26 nm. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders contained mixtures of Nd4Ti9O24, Nd2Ti4O11, Nd3Ti4O12 for titanium dominant powders (Nd:Ti ≤ 45:60), mixtures of Nd2TiO5 and Nd2O3 for neodymium dominant powders (Nd:Ti ≥ 75:25) and pure Nd3Ti4O12 phase for equal molar ratio of Nd:Ti, depending on the annealing temperature and Nd:Ti...