Nanostructured molybdenum oxide was potentiodynamically deposited onto a stainless steel surface from an aqueous bath by cycling the potential between 0 and -0.75 V vs. Ag/AgCl. The deposit consisted of particulates in the range of 30 to 80 nm. Electrochemical studies under galvanostatic charge/discharge and also impedance spectroscopy revealed capacitive behavior in the potential range of -0.3 to -0.55 V vs. Ag/AgCl with the value of 477 F g-1 at 0.1 mA/cm2. An equivalent circuit comprising of three parallel branches consisting of double-layer capacitance, Warburg impedance, and a constant phase element signifying pseudo-capacitance each coupled with their corresponding resistances was... 

In this work, graphene oxide (GO) aqueous suspensions prepared by a chemical exfoliation method showed a fluorescence peak at ∼615 nm. Photoluminescence spectroscopy determined that functionalization of the GO sheets by 3-(2-Aminoethylamino) propyltrimethoxysilane molecules significantly quench the fluorescence property of the GO sheets. Fourier transform infrared spectroscopy confirmed proper functionalization of the GO sheets. Curcumin was applied as a fluorescent natural material with an emission peak at ∼550 nm wavelength for green fluorescent labeling of the functionalized-GO sheets. The curcumin-labeled functionalized-GO sheets showed an intense emission band fluorescent property with... 

Undoped and copper doped nanostructured zinc oxides were synthesized by using a series of synthetic layered material, undoped and copper doped zinc hydroxide nitrates at various molar percentages of copper (2-10) within the layers as precursors. The layered materials were heat-treated at 500 °C to produce zinc oxide nanostructures with crystallite sizes in the range of 23-35 nm. Optical studies of the nanostructured copper doped zinc oxides showed the decrease in band gap with increasing content of the doping agent, copper  

Nanostructured molybdenum oxide having a particle size in the range of 30-80 nm was prepared by potentiodynamic electrodeposition method, and the effects of H2SO4 concentration on its capacitive behavior were studied by cyclic voltammetry, galvanostatic discharge, and electrochemical impedance spectroscopy. Poor to fair capacitive behaviors were witnessed depending on the electrolyte concentration and conditions of charge/discharge. Increasing acid concentration to 0.02 M had favorable effect, while beyond that, the effect was detrimental. Capacitance around 600 F g-1 was recorded in the potential range of 0 to -0.55 V vs. Ag/AgCl  

Heterogeneous nanoscale catalyst was successfully synthesized via anchoring of oxoperoxo molybdenum(VI) complex on the chloro-functionalized SBA-15. The mesoporous nanomaterials, MoO3(sal-phz)/SBA-15 (where sal-phz is salicylidene 2-picoloyl hydrazine) were identified by several characterization techniques. MoO3(sal-phz)/SBA-15 and MoO3(sal-phz) were also treated as catalysts in the olefins epoxidation reactions. Both homogenous and heterogeneous catalysts exhibit outstanding activity and selectivity for epoxide with tert-BuOOH in decane as oxidant at 95 °C. In addition, the heterogeneous nanocatalyst was chemically stable and can be efficiently reused for at least six cycles without a... 

Porous network-like MnO2 thick films are successfully synthesized on a flexible stainless steel (SS) mesh using a simple and low-cost electrodeposition method followed by an electrochemical activation process. Morphology, chemical composition, and crystal structure of the prepared electrodes before and after the activation process are determined and compared by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), and X-ray diffraction (XRD) analyses. The results show that the implementation of the electrochemical activation process does not change the chemical composition and crystal structure of the films, but it influences the surface morphology of the MnO2... 

To improve the efficiency of electrochemical processes for environmental remediation, we present a new type of hybrid nanomaterials based on leaf-like copper-based quaternary transition metals and spongy monolayer graphene. To demonstrate the functionality of the hybrid electrocatalyst, fast and competent electrooxidation of water and glucose is shown. The mechanism of improved catalysis is ascribed to the synergetic catalytic effect of quaternary Cu-Ni-Fe-Co alloy with dendritic morphology along with the highly conductive and spongy structure of the graphene monolayer. It is shown that water oxidation can be performed at a low overpotential of 315 mV to reach a current denisty of 100 mA... 

Co-free Li-rich manganese nickel oxide (LMNO) materials are emerging as an up-and-coming candidate for high-energy–density cathodes. However, they suffer from severe cycling capacity fading and poor performance rates. Herein, the surface functionalization of an LMNO cathode is designed by polypyrrole (PPy) nanostructure coating. We found that PPy nanoparticles@LMNO cathode exhibits high-capacity retention and enhanced rate capabilities, delivering a discharge capacity as high as 191 mAh g−1, with capacity retention of 96%, after ∼ 200 cycles at a current density of 20 mA g−1. The results indicate that the intercalation and doping pseudocapacitance can be varied depending on the synthesis... 

Micro arc oxidation was employed to grow TiO2/hydroxyapatite composite layer on titanium substrate. The correlation between electrolyte concentration, diameter and density of the pores in fabricated layers was investigated. Therefore, the effect of electrolyte concentration on composition and morphology of grown layers was studied using SEM, EDX, XRD and XPS techniques. Samples were coated in electrolytes containing 5, 10 and 15 g/l calcium acetate and 1, 3 and 5 g/l β-glycerophosphate, at optimized voltage for 3 min. Pore size variations obey a similar pattern by the addition of both calcium acetate and β-glycerophosphatein various concentrations based on SEM observations. However,... 

In this study, two different chemical solution methods were used to synthesize Zinc oxide nanostructures via a simple and fast microwave assisted method. Afterwards, the photocatalytic performances of the produced ZnO powders were investigated using methylene blue (MB) photodegradation with UV lamp irradiation. The obtained ZnO nanostructures showed spherical and flower-like morphologies. The average crystallite size of the flower-like and spherical nanostructures were determined to be about 55 nm and 28 nm, respectively. X-ray diffraction (XRD), scanning electronic microscopy (SEM), Brunauer-Emmett-Teller (BET), room temperature photoluminescence (RT-PL) and UV-vis analysis were used for... 

Through a fast, simple, low cost, surfactant-free and convenient microwave-assisted route, narcis-like ZnO nanostructures (10-15 nm size) with flower diameters in the range of 1-2.5 μm were synthesized. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) spectroscopy and room temperature photoluminescence (PL) measurements were used to characterize the produced ZnO nanostructures. The principle raw materials - ammonium hydroxide (NH4OH) and zinc acetate dihydrate [Zn(CH3COO)2·2H2O] - were both inexpensive. The method was fast, simple and surfactant-free capable of producing larger quantities of zinc oxide... 

In this work, we study the role of nanotextured ZnFe2O4/Fe2O3composite thin films fabricated by ultrasonic spray pyrolysis (USP) on the photoelectrochemical water oxidation reactions. The ZnFe2O4/Fe2O3 composites with different molar ratios are deposited on three-dimensional nanospikes (NSP) substrate, and the results are compared with those for planar devices. It is observed that optical absorption and charge separation due to larger surface area is significantly enhanced in nanotextured photoactive ZnFe2O4/Fe2O3 films. After characterization of ZnFe2O4/Fe2O3 composite films with different molar ratios (ZF1, ZF2, and ZF3), we find that the nanotextured ZF1 composite with a molar ratio of... 

Evolution of renewable energies in the era of the modernized world has been strongly tied up to the incessant development of high-performance energy storage systems benefiting from both high energy and power densities. In the present work, binder-free positive electrodes are fabricated via a facile electrochemical deposition route in which copper oxide nanorods (CuO NRs) directly grown onto the copper foam (CF) are decorated with bimetallic cobalt-zinc sulfide nanoarrays (Co-Zn-S NAs). The fabricated Co-Zn-S@CuO-CFs represent promising specific capacity of 317.03 C.g−1 at 1.76 A.g−1, along with superior cyclic stability (113% retention after 4500 cycles). Negative electrodes were further... 

Evolution of renewable energies in the era of the modernized world has been strongly tied up to the incessant development of high-performance energy storage systems benefiting from both high energy and power densities. In the present work, binder-free positive electrodes are fabricated via a facile electrochemical deposition route in which copper oxide nanorods (CuO NRs) directly grown onto the copper foam (CF) are decorated with bimetallic cobalt-zinc sulfide nanoarrays (Co-Zn-S NAs). The fabricated Co-Zn-S@CuO-CFs represent promising specific capacity of 317.03 C.g−1 at 1.76 A.g−1, along with superior cyclic stability (113% retention after 4500 cycles). Negative electrodes were further... 

Molybdenum oxide nanostructures were synthesized utilizing the solution combustion method where the ammonium molybdate powder and an organic additive were used as precursors. Different organic additives including ethylene diamine tetraacetic acid (EDTA), polyethylene glycol 200 (PEG 200), sorbitol and urea were used as surfactants in order to investigate the effect of additive structure on morphology and particle size of products. Also various reaction parameters such as the additive/Mo molar ratio, concentration of metal ion in solution, pH of the reaction, and temperature of the synthesis media were changed to study effects on product morphology and size. Outcomes were characterized by... 

Nowadays, putting forward an accurate cancer therapy method with minimal side effects is an important topic of research. Nanostructures, for their ability in controlled and targeted drug release on specific cells, are critical materials in this field. In this study, a pH-sensitive graphene oxide-l-arginine nanogel was synthesized to carry and release 5-fluorouracil. Optimized conditions using statistical analysis, based on the maximum relative viscosity of nanogel, were evaluated: 5.489 for the concentration of l-arginine and 2.404 for pH. The prepared nanogels were characterized using scanning electron microscope and transmission electron microscope images and Fourier-transform infrared...