Sharif Digital Repository

In this work, cristobalite crystallization and its effects on mechanical and chemical behaviour of injection moulded silica-based ceramic cores were investigated. In order to simulate casting process condition, the sintered samples at 1220 °C were also heated up to 1430 °C. Flexural strength test was carried out on both sintered and heat treated samples. Chemical resistance of the cores was evaluated by leaching the samples inside 43. wt% KOH solution at its boiling point. Phase evolution and microstructure were investigated by thermal analyses (DTA and DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM) and optical microscopy (OM). Results showed that cristobalite was... 

In this work, phase evolution, solid solution formation and diffusion behavior of three binary systems, including TaC-HfC, TaC-ZrC and HfC-ZrC, were investigated. In this regard, pure carbide powders of TaC, HfC, and ZrC were selected as starting raw materials. The prepared samples were heat treated at 2000 C for 1 hour in Ar atmosphere. For each system, three compositions were chosen for phase evolution investigation by X-ray diffractometer. Moreover, three couple samples were prepared for diffusion behavior survey through SEM/EDX analyses. It was found that ZrC diffuses faster in TaC structure rather than HfC and a single phase solid solution phase with hosting TaC is formed in TaC-HfC and... 

In the current research, a cost-effective and modified method with a high degree of reproducibility was proposed for the preparation of fine nanoscale and high-purity BaTiO3. In contrast to the other established methods, in this research, carbonate-free BaTiO3 nanopowders were prepared at a lower temperature and in a shorter time span. To reach an in-depth understanding of the scientific basis of the proposed process, an in-detail analysis was carried out for characterization of nanoscale BaTiO3 particles via differential thermal analysis (DTA)/thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and...