In this study, we explore resonance-enhanced optical absorption in Ta 3N5 photoanodes for water splitting. By using a reflecting Pt back-contact and appropriate Ta3N5 film thickness, the resonance frequency can be tuned to energies just above the bandgap, where the optical absorption is normally weak. The resonance results in a significant improvement in the photoanode's incident photon-to-current efficiency. The Ta3N5 films are made by high-temperature nitridation of Ta2O5. The nitridation time is found to be critical, as extended nitridation result in the formation of nitrogen vacancies through thermal reduction. These insights give important clues for the development of efficient... 

Providing solar hydrogen as a clean energy resource is one of the human challenges for future. Controlling oxygen vacancies as well as surface morphology in metal oxide semiconductors enables developing PEC H2production in some understood ways. Here, the influence of simple change in annealing atmosphere, air and pure oxygen, on photoresponse of nanocrystalline WO3has been studied completely. Results revealed that such slight change in annealing procedure increases effective surface interface and donor density by 77 and 72%, respectively. These effects and also retarding recombination of photogenerated electro-hole pair resulted in photocurrent enhancement under solar like illumination more... 

Although hematite (i.e., α-Fe2O3) has been widely investigated in photoelectrochemical water oxidation studies due to its high theoretical photocurrent density, it still suffers from serious surface charge recombination and low photoelectrochemical stability. Here we report an in situ electrochemical method to form a uniform and ultrathin (i.e., 3-5 nm) passivation layer all over the pores of an optimized ∼3.2% Ti-doped α-Fe2O3 photoanode. We unveil the amorphous and defective nature of the in situ derived layer assigned to a high concentration of oxygen vacancies and intercalated potassium atoms there, i.e., the formation of Ti/K co-doped defective α-Fe2O3−x. Owing to the efficient... 

Morphology tailored TiO2 nano assemblies consisting of nanorods with and without nanoparticle attachments were hydrothermally synthesized and their characteristics and light scattering properties were determined by x-ray diffraction (XRD), nitrogen sorption analysis, scanning electron microscopy (SEM), transmission electron microscopy (TEM), electrochemical impedance spectroscopy (EIS) and ultraviolet-visible spectroscopy (UV-Vis). The nanorod-nanoparticles (NR-NP) assemblies and smooth nanorod (NR) double layers were screen printed onto fluorine doped tin oxide coated glass underlayers to fabricate dye-sensitized solar cell (DSSC) photoanodes. The double layer heterogeneous... 

In this research TiO2 nanocrystals with sizes about 11-70 nm were grown by hydrothermal method. The process was performed in basic autoclaving pH in the range of 8.0-12.0. The synthesized anatase phase TiO2 nanocrystals were then applied in the phtoanode of the dye sensitized solar cells. It was shown that the final average size of the nanocrystals was larger when the growth was carried out in higher autoclaving pHs. The photoanodes made of TiO2 nanocrystals prepared in the pHs of 8.0 and 9.0 represented low amounts of dye adsorption and light scattering. The performance of the corresponding dye sensitized solar cells was also not acceptable. Nevertheless, the energy conversion efficiency... 

Different compositions of TiO2–BaTiO3 nanocomposites are synthesized with various weight ratios for dye-sensitized solar cell (DSSC) applications. TiO2 and BaTiO3 nanoparticles (NPs) are synthesized by sol-gel and solvothermal methods, respectively and are employed as the photoanode electrodes. BaTiO3 NPs have pure cubic perovskite crystal structure with an average size of 20-40 nm, while TiO2 NPs show pure anatase phase with 15-30 nm size. The power conversion efficiency (PCE) enhancement of the cells is first attained by controlling the thickness of the films for light harvesting improvement. The fabricated DSSC composed of pure BaTiO3 NPs with an optimal thickness of 25 μm shows... 

TiO2 nanotube arrays (TNA) have been modified by cobalt phosphate (CoPi) through potentiostatic electrodeposition method. Different samples have been prepared by changing the loaded CoPi through the deposition time from 10 to 960 min. Formed catalytic materials have been characterized by different methods. Although charge transfer resistance of the CoPi/TNA photoanodes have been decreased from 5.5 to 4.0 kΩ by increasing the deposition time from 5 to 60 min, the maximum photoresponse was obtained for 10 min CoPi deposition leading to 24% more photocurrent compare to bare TNA which proposed optimum value for cobalt phosphate decoration. Based on field emission scanning electron microscopy... 

Here, a solution combustion method was employed to construct a photoanode based on bismuth vanadate (BV) composition. To curtail the fast charge recombination, phosphorus-doped g-C3N4 nanosheets (PCNS) in combination with BV are considered a potential approach. The prepared solution combustion facilitated the formation of a BiVO4-PCNS (BV-PCNS) hybrid photoanode with worm-like morphology with a simple setup. The weight ratio of PCNS/BiVO4 and the loading volume/cm2 were optimized to determine the most efficient photoanode. The highest photocurrent density of 0.5 mA/cm2 at 1.23 V vs reversible hydrogen electrode (RHE) under 1 sun illumination was achieved for the hybrid nanostructure at 2 wt... 

WO3 thin film photoanodes containing different concentrations of Ag nanoparticles were synthesized by solegel method. Based on UV-visible spectra, presence of a surface plasmon resonance peak at 470 nm of wavelength indicated formation of silver nanoparticles in the WO3 films. According to atomic force microscopy (AFM) analysis, the highest value for surface roughness and the effective surface ratio was observed for the sample containing 2 mol% of Ag. X-ray diffraction (XRD) patterns revealed that WO 3 nanocrystalline structure was formed in the monoclinic phase with the average size of about 18.2 nm while Ag nanocrystals were determined in cubic phase. X-ray photoelectron spectroscopy (XPS)... 

Here we analyze the effect of two relevant aspects related to cell preparation on quantum dot sensitized solar cells (QDSCs) performance: the architecture of the TiO 2 nanostructured electrode and the growth method of quantum dots (QD). Particular attention is given to the effect on the photovoltage, V oc, since this parameter conveys the main current limitation of QDSCs. We have analyzed electrodes directly sensitized with CdSe QDs grown by chemical bath deposition (CBD) and successive ionic layer adsorption and reaction (SILAR). We have carried out a systematic study comprising structural, optical, photophysical and photoelectrochemical characterization in order to correlate the material... 

TiO 2 nanorods, TiO 2 nanorod/TiO 2 nanoparticle and TiO 2 nanorod/ZnO nanoparticle composite structures were integrated as photoanodes in backside illuminated dye-sensitized solar cells (DSSCs). Incorporation of TiO 2 nanoparticles into the bare nanorods increased the dye loading and improved the short-circuit current density (J sc) from 2.22 mA/cm 2 to 3.57 mA/cm 2. ZnO nanoparticles electrochemically grown into the TiO 2 nanorod layer could increase the surface area. Nevertheless, this considerably reduced the J sc to 0.57 mA/cm 2 and consequently cell efficiency. Electrochemical impedance spectroscopy (EIS) results showed that ZnO incorporated samples have better effective diffusion... 

Nanoparticulated TiO 2 fibers as one-dimensional long structures were introduced into TiO 2 P25 nanoparticle films using coelectrophoretic deposition. This prevented the usual crack formation occurring in wet coatings, and resulted in less porosity and higher roughness factor of the films that provided more favorable conditions for electron transport. The films used as the photoanode of a dye solar cell (DSC) produced 65% higher photovoltaic efficiency. TiO 2 fibers can be excellent binders in single-step, organic-free electrophoretic deposition of TiO 2 for DSC photoanode  

In this study, pure TiO2 and Au:TiO2 nanocomposite thin films are both synthesized using sol-gel and RF reactive co-sputtering methods. Physical and photoelectrochemical properties of the thin films deposited by each method are compared. The optical density spectra and scanning electron microscopy images of the Au:TiO2 films reveal formation of gold nanoparticles in the all nanocomposite films synthesized by two methods. Moreover, the optical bandgap energy of the thin films decreases with addition of Au nanoparticles. X-ray photoelectron spectroscopy indicates that the presence of gold in metallic state and the formation of TiO2 is stoichiometric. The photoelectrochemical properties of the... 

In this investigation, the effect of annealing temperature and concentration of gold nanoparticles on the photoelectrochemical properties of sol-gel deposited Au : TiO2 nanocomposite thin films is studied. Various gold concentrations have been added to the TiO2 thin films and their properties are compared. All the deposited samples are annealed at different temperatures. The optical density spectra of the films show the formation of gold nanoparticles in the films. The optical bandgap energy of the Au : TiO2 films decreases with increasing Au concentration. The crystalline structure of the nanocomposite films is studied by x-ray diffractometry indicating the formation of gold nanocrystals in...