Sharif Digital Repository

Lead sulfide quantum dots (PbS QDs) were decorated onto a graphene surface in a semi-core-shell structure using supercritical ethanol. The temperature of ethanol played significant role in controlling size and agglomeration of QDs as well as the extent of reduction of graphene. Average size of the QDs was estimated by transmission electron microscopy to be around 3.96 nm and by quantum models to be about 4.34 nm. PbS QDs prepared at 330 °C were of high purity, and the yield was 99%. Instrumental and chemical analyses demonstrated formation of a strong bond between PbS QDs and graphene, through a Pb-O-C bridge. UV and photoluminescence measurements along with theoretical considerations... 

Rather vertically aligned ZnO rods with flower-like structures were grown on quartz substrates through vapor phase transport method. X-ray diffraction (XRD) analysis and photoluminescence (PL) measurement were performed to determine crystalline structure and defects, respectively. H2S gas sensing properties of the grown structure were investigated at both room temperature and 250 °C for comparison. A remarkable increase in response and selectivity at room temperature compared to 250 °C was observed. High response and selectivity to low concentrations of H2S at room temperature as well as good stability make the sensor a promising candidate for practical applications  

Ferrite nanocrystals are an interesting material due to their rich physical properties. Here we add nonmagnetic dopants Zn and Cu to nickel ferrite nanocrystals, Ni1-xMxFe2O4 (0 ≤ x ≤ 1, M = Cu, Zn), and study how relevant properties of the samples are modified accordingly. Basically, these dopings cause a rearrangement of Fe +3 ions into the two preexisting octahedral and tetrahedral sites. In fact, this, we show, induces pertinent magnetic properties of the doped samples. In the case of the Cu-doping, the Jahn-Teller effect also emerges, which we identify through the Fourier Transform Infra-Red Spectroscopy of the samples. Moreover, we show an increase in the lattice parameters of the... 

Solution-processed quantum dots (QDs) have attracted significant attention for the low-cost fabrication of optoelectronic devices. Here, we synthesized PbS QDs via hot injection method and passivated the trap states by using short thiols and dopant elements for photovoltaic application. In order to study the effect of dopants on photovoltaic application, PbS QDs were doped by using three different cations: Cadmium, Calcium, and Zinc. We utilized Time resolvel Photoluminescence measurement to study the carriers lifetime for different samples and found that the carriers life time increases ∼80% by using Cd as a dopant compared with undoped sample. In addition, the results of J-V measurement... 

In this work we report a fast two-step microwave activated synthesis of the ZnS:Mn nanocrystals. Zn(NO3)2 and Na2S 2O3 were used as the precursors and Mn(NO 3)2 was employed as the source of the impurity. The aqueous synthesis was based on the heat sensitivity of Na2S 2O3, which releases some S species on heating. Consequently, the reaction was well activated under microwave irradiation resulting in formation of ZnS:Mn nanocrystals. Thioglycerol (TG) was also used as the capping agent and the catalyst of the reaction. The synthesis process was done in two steps, i.e. 1 min irradiation without TG and then injection of TG and continuation of irradiation. ZnS:Mn nanocrystals were quickly formed... 

The g-C3N4/Fe2O3 nanocomposite was produced by the solution combustion synthesis (SCS) of iron-nitrate/g-C3N4 mixtures of varying concentration ratios and using urea as a fuel. The following methods did characterization of the products: X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), Fourier-transform infrared spectroscopy (FTIR), Brunauer-Emmett-Teller investigation (BET), ultraviolet–visible light analysis (UV–vis) and photoluminescence measurement (PL). Effect of iron nitrate on stability and photocurrent density under simulated visible-light irradiation was determined. The...