In this research MPA capped CdTe nanocrystals with sizes around 2.7-3.5 nm were grown in aqueous solution. The process was performed through the reaction of NaHTe with MPA and CdCl2 solution in high temperature. The synthesis was carried out in two different states of standard and modified forms. In the modified synthesis, the hydrazine hydrate material was added to the MPA plus CdCl2 solution before injection. The evolution of the nanocrystals size and PL quantum yield was monitored during the heating time for the growth. The results demonstrated that for the standard synthesis the growth rate was slow. The CdTe nanocrystals with high PL quantum yields were achieved in more than 10 h of... 

We have synthesized CdS NCs (NCs) by a thermochemical approach. CdSO 4 and Na2S2O3 were used as the precursors and thioglycolic acid (TGA) was used as capping agent molecule. The structure and optical property of the NCs were characterized by means of XRD, TEM, UV-visible optical spectroscopy and photoluminescence (PL). XRD and TEM analyses demonstrated hexagonal phase CdS NCs with an average size of around 2 nm. Synthesized NCs exhibited a band gap of about 3.21 eV and showed a broad band emission from 400 to 750 nm centered at 503 nm. This broad band emission is related to surface states of CdS and our results showed that the emission peak can be attributed to the interstitial sulfur. The... 

Perovskite solar cells suffer from various instabilities on all time scales. Some of them are driven by light, in particular when employing compounds with mixed halides. Such light soaking effects have been observed to result in performance changes of solar-cell devices. They have also been spectroscopically investigated in detail on films, where the formation of a low-gap iodine-rich phase, seen as a red shift of the PL, has been found to be responsible for a reduced open-circuit voltage. However, studies synchronously examining device performance and its relation to spectroscopy data are scarce. Here, we perform an in operando study, where we investigate the changes of open-circuit voltage... 

We have synthesized CdS nanocrystals (NCs) by a microwave activated method. CdSO4 and Na2S2O3 were used as the precursors and thioglycolic acid (TGA) was used as capping agent molecule. The aqueous synthesis was based on the heat sensitivity of Na2S 2O3. In this method, microwave irradiation creates the activation energy for dissociation of Na2S2O3 and leads to the CdS NCs formation. X-ray diffraction (XRD) and transmission electron microscopy (TEM) analyses demonstrated hexagonal phase CdS NCs with an average size around 3 nm for sample prepared at 5 min irradiation time. A band gap range of 3.38-2.89 eV was possible only by increasing the microwave irradiation time, corresponding to a...