Pure Zn and Zn matrix composite coatings containing nano-sized SiC particles with an average size of 50 nm were prepared from the zinc sulfate bath. The effects of the pulse frequency, maximum current density and duty cycle on the amount of particles embedded were examined. Electron microscopic studies revealed that the coating morphology was modified by the presence of SiC nanoparticles. In the presence of SiC nanoparticles deposit grows in outgrowth mode resulting in a very rough and porous microstructure. However, at very low and very high duty cycles a smooth and pore free microstructure was obtained. Corrosion resistance properties of the coatings were studied using potentiodynamic... 

The adhesion of hydroxyapatite (HA) as a coating for the AZ91 magnesium alloy substrate can be improved by using the sputtering method and an intermediate layer, such as ZrN. In this study, HA coatings were applied on ZrN intermediate layers at a temperature of 300 °C for 180, 240, 300, 360, and 420 min by ion beam sputtering. A profilometer device was used to study the HA coating thickness, which changed from 2 μm for the 180-min deposition to 4.7 μm for 420-min deposition. The grazing incidence X-ray diffraction analysis method and the Williamson–Hall analysis were used for structural investigation. As the deposition time increased, the crystalline size increased from 50 nm to 690 nm.... 

In this research, submicron bioactive glass (BG) particles were synthesized by a sol-gel process and were then coated on a 316L stainless steel substrate using an electrophoretic deposition (EPD) technique. Stable suspension of bioactive glass powders in ethanol solvent was prepared by addition of triethanol amine (TEA), which increased zeta potential from 16.5 ± 1.6 to 20.3 ± 1.4 (mv). Thickness, structure and electrochemical behavior of the coating were characterized. SEM studies showed that increasing EPD voltage leads to a coating with more agglomerated particles, augmented porosity and micro cracks. The results of Fourier transformed infrared (FTIR) spectroscopy revealed the adsorption...