The effect of pulse reverse current (PRC) method on Ni-Mo coatings electroplated from chloride solution was investigated by various plating parameters such as plating duration, the anodic duty cycle, the anodic current density and the cathodic current density. By increasing the anodic duty cycle and anodic current density, the Mo content of coatings reached 68wt.% and 78wt.%, respectively at cathodic current densities of 500 and 300mAcm-2. The Mo content of coatings increases by the preferential dissolution of Ni on the anodic pulse and also by the replenishment of Mo complexes in the diffusion layer near the substrate surface during the anodic pulse. In comparison with the direct current... 

The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the deposition current density. The corrosion resistance of the deposits was studied and compared with that of monolayers of Ni-P and Zn-Ni alloys via Tafel polarization, EIS and salt spray tests. Characterization of corrosion products by means of EDS and XRD revealed more details from the corrosion mechanism of the monolayers and multilayers. The corrosion current density of Ni-P/Zn-Ni CMMCs were around one tenth of Zn-Ni monolayer. The CMMC with incomplete layers performed lower polarization resistance and higher corrosion current density compared to the CMMC with...